Hydrogel contact lens having wet surface, and manufacturing method therefor
The present invention relates to a hydrogel contact lens having a wet surface, and a manufacturing method therefor and, more specifically, to a hydrogel contact lens and a manufacturing method therefor wherein the hydrogel contact lens satisfies basic physical properties of a hydrogel contact lens and has excellent wettability by forming a hydrophilic surface layer of an interpenetrating polymer network (IPN) structure on a surface of the hydrogel contact lens.
1. A manufacturing method for a hydrogel contact lens comprising a hydrogel contact lens substrate and a hydrophilic surface layer having an interpenetrating polymer network (IPN) structure formed on a surface of the hydrogel contact lens substrate, comprising:
a first step of preparing the hydrogel contact lens substrate; and
a second step of immersing the hydrogel contact lens substrate for at least 1 hour in a single surface-modifying solution including 0.05 to 2 wt % of a sodium hyaluronate compound, 0.2 to 10 wt % of a hydrophilic monomer, a crosslinking agent having a content of 0.001 to 0.1 mol per 1 mol of the hydrophilic monomer, 0.001 to 0.5 wt % of an initiator, and a residual content of water,
wherein a physical intermixed layer with the hydrophilic surface layer is formed in the contact lens substrate to have a thickness of 20 nm or more, and
wherein the hydrophilic surface layer having the interpenetrating polymer network (IPN) structure is formed from a single mixture including the sodium hyaluronate compound, the hydrophilic monomer, and the crosslinking agent.
2. The manufacturing method of claim 1 , further comprising:
swelling the hydrogel contact lens substrate that is performed between the first step and the second step.
3. The manufacturing method of claim 2 , wherein the swelling is performed by immersing the hydrogel contact lens substrate in an alcohol solution.