Thermoplastic resin composition containing polycarbonate resin, graft copolymer, and copolymer, and molded article thereof
A thermoplastic resin composition includes 10 to 95 parts by weight of a polycarbonate resin (A); 5 to 90 parts by weight of a graft copolymer (B); and 0 to 50 parts by weight of a copolymer (C). The graft copolymer (B) is produced by the graft polymerization of 10 to 80 parts by weight of a rubbery polymer with 20 to 90 parts by weight of a monomer component including an aromatic vinyl monomer and/or a cyanide vinyl monomer, wherein the rubbery polymer has a weight average particle size of 150 to 450 nm and also has a 10 wt % particle size of 50 to 250 nm and a 90 wt % particle size of 450 to 650 nm in a particle size cumulative weight fraction. The copolymer (C) is produced by copolymerizing an aromatic vinyl monomer, a cyanide vinyl monomer and another vinyl monomer with one another.
1. A thermoplastic resin composition, comprising:
30 to 60 parts by weight of a polycarbonate resin (A),
20 to 60 parts by weight of a graft copolymer (B), and
10 to 20 parts by weight of a copolymer (C) wherein the total is 100 parts by weight,
the graft copolymer (B) being a graft copolymer obtained by graft polymerizing 20 to 90 parts by weight of at least one monomer including at least an aromatic vinyl monomer and/or a vinyl cyanide monomer to 10 to 80 parts by weight of alkyl(meth)acrylate rubber having a weight average particle size of 150 to 450 nm and having a particle size for a cumulative weight fraction of 10 wt % of 50 to 150 nm and a particle size for a cumulative weight fraction of 90 wt % of 450 to 650 nm (wherein a total of the alkyl(meth)acrylate rubber and the monomer(s) is 100 parts by weight); and
the copolymer (C) being a copolymer obtained by polymerizing a monomer mixture including 60 to 95 wt % of an aromatic vinyl monomer, 5 to 40 wt % of a vinyl cyanide monomer, and 0 to 40 wt % of an additional monomer copolymerizable with said monomers, and a weight average molecular weight (Mw) of the copolymer (C) being in a range of 50000 to 200000.
2. The thermoplastic resin composition according to claim 1 , wherein the alkyl(meth)acrylate rubber in the graft copolymer (B) is obtained by adding a condensed acid salt to a latex of a rubbery polymer with a small particle size and thereafter mixing the latex with an acid group-containing copolymer latex to enlarge the particle size.
3. The thermoplastic resin composition according to claim 2 , wherein an amount of the condensed acid salt added is 0.1 to 10 parts by weight with respect to 100 parts by mass (in terms of solids) of the latex of the rubbery polymer with the small particle size, and an amount of the acid group-containing copolymer latex is 0.1 to 10 parts by mass (in terms of solids) with respect to 100 parts by mass (in terms of solids) of the latex of the rubbery polymer with the small particle size.
4. The thermoplastic resin composition according to claim 2 , wherein the acid group-containing copolymer latex is obtained by polymerizing a monomer mixture including an acid group-containing monomer, an alkyl (meth)acrylate ester monomer and optionally an additional monomer copolymerizable with these monomers.
5. The thermoplastic resin composition according to claim 1 , wherein a composition of the monomers to be graft polymerized to the alkyl(meth)acrylate rubber to form the graft copolymer (B) is one selected from the group consisting of:
60 to 90 wt % aromatic vinyl monomer, 10 to 40 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer;
30 to 80 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, and 0 to 50 wt % copolymerizable additional vinyl monomer; and
20 to 70 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, 10 to 60 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer.
6. The thermoplastic resin composition according to claim 1 , wherein the graft copolymer (B) has a graft ratio of 5 to 150% and the reduced viscosity of 0.2 to 2.0 dL/g.
7. A molded article obtained by molding the thermoplastic resin composition according to claim 1 .
8. The thermoplastic resin composition according to claim 3 , wherein the acid group-containing copolymer latex is obtained by polymerizing a monomer mixture including an acid group-containing monomer, an alkyl (meth)acrylate ester monomer and optionally an additional monomer copolymerizable with these monomers.
9. The thermoplastic resin composition according to claim 2 , wherein a composition of the monomers to be graft polymerized to the alkyl(meth)acrylate rubber to form the graft copolymer (B) is one selected from the group consisting of:
60 to 90 wt % aromatic vinyl monomer, 10 to 40 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer;
30 to 80 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, and 0 to 50 wt % copolymerizable additional vinyl monomer; and
20 to 70 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, 10 to 60 wt % vinyl cyanide monomer, and (1 to 30 wt % copolymerizable additional vinyl monomer.
10. The thermoplastic resin composition according to claim 3 , wherein a composition of the monomers to be graft polymerized to the alkyl(meth)acrylate rubber to form the graft copolymer (B) is one selected from the group consisting of:
60 to 90 wt % aromatic vinyl monomer, 10 to 40 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer;
30 to 80 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, and 0 to 50 wt % copolymerizable additional vinyl monomer; and
20 to 70 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, 10 to 60 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer.
11. The thermoplastic resin composition according to claim 4 , wherein a composition of the monomers to be graft polymerized to the alkyl(meth)acrylate rubber to form the graft copolymer (B) is one selected from the group consisting of:
60 to 90 wt % aromatic vinyl monomer, 10 to 40 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer;
30 to 80 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, and 0 to 50 wt % copolymerizable additional vinyl monomer; and
20 to 70 wt % aromatic vinyl monomer, 20 to 70 wt % (meth)acrylate ester monomer, 10 to 60 wt % vinyl cyanide monomer, and 0 to 30 wt % copolymerizable additional vinyl monomer.
12. The thermoplastic resin composition according to claim 2 , wherein the graft copolymer (B) has a graft ratio of 5 to 150% and the reduced viscosity of 0.2 to 2.0 dL/g.
13. The thermoplastic resin composition according to claim 3 , wherein the graft copolymer (B) has a graft ratio of 5 to 150% and the reduced viscosity of 0.2 to 2.0 dL/g.
14. The thermoplastic resin composition according to claim 4 , wherein the graft copolymer (B) has a graft ratio of 5 to 150% and the reduced viscosity of 0.2 to 2.0 dL/g.
15. The thermoplastic resin composition according to claim 5 , wherein the graft copolymer (B) has a graft ratio of 5 to 150% and the reduced viscosity of 0.2 to 2.0 dL/g.
16. A molded article obtained by molding the thermoplastic resin composition according to claim 2 .
17. A molded article obtained by molding the thermoplastic resin composition according to claim 3 .
18. A molded article obtained by molding the thermoplastic resin composition according to claim 4 .
19. A molded article obtained by molding the thermoplastic resin composition according to claim 5 .
20. The thermoplastic resin composition according to claim 1 , wherein the thermoplastic resin comprises 30 parts by weight of the polycarbonate resin (A).