Coated metal sheet, method for manufacturing same, and exterior building material
Provided is a coated metal sheet for exterior use, having a metal sheet, and a top coat film situated on the metal sheet. The top coat film contains a resin, 0.2-15 volume percent of a gloss control agent composed of porous particles, and a delustering agent composed of primary particles. The coated metal sheet satisfies the following expressions in which, in the number-size distribution of the gloss control agent and the delustering agent, R is the number-average particle diameter (μm) of the gloss control agent, D1 97.5 and D2 97.5 are 97.5% particle diameter values (μm) of the gloss control agent and the delustering agent, Ru is the upper limit particle diameter (μm) of the gloss control agent, and T is the film thickness (μm) of the top coat film. D 1 97.5 /T ≤0.7 Ru ≤1.2 T R ≥1.0 2.0≤ D 2 97.5 /T ≤7.0 13≤ T ≤20.
1. A coated metal sheet comprising:
a metal sheet, and
an overcoat coating film disposed on the metal sheet,
wherein the overcoat coating film comprises a resin, a gloss adjusting agent which is particles having micropores, and a matting agent which is primary particles,
wherein a content of the gloss adjusting agent in the overcoat coating film is from 0.2 to 15 vol %,
wherein a content of the matting agent in the overcoat coating film is from 0.2 to 15 vol %, and
wherein the coated metal sheet satisfies the following equations:
D 1 97.5 /T≤ 0.7
Ru≤ 1.2 T
R≥ 1.0
2.0≤ D 2 97.5 /T≤ 7.0
13≤ T≤ 20
wherein R (μm) is a number average particle diameter of the gloss adjusting agent, T (μm) is a film thickness of the overcoat coating film, D1 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the gloss adjusting agent based on the number of particles, D2 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the matting agent based on the number of particles, and Ru (μm) is an upper limit particle diameter in a number particle size distribution of the gloss adjusting agent.
2. The coated metal sheet according to claim 1 , further comprising an undercoat coating film between the metal sheet and the overcoat coating film.
3. The coated metal sheet according to claim 1 , wherein the Ru is less than T.
4. The coated metal sheet according to claim 1 , wherein the metal sheet has been subjected to non-chromate anti-rust treatment, and the coated metal sheet is chromate-free.
5. The coated metal sheet according to claim 1 , wherein the metal sheet has been subjected to chromate anti-rust treatment.
6. The coated metal sheet according to claim 1 , wherein the gloss adjusting agent is silica particles.
7. The coated metal sheet according to claim 1 , having a glossiness at 75° is 1 to 25.
8. The coated metal sheet according to claim 1 , being a coated metal sheet for exterior use.
9. An exterior building material composed of the coated metal sheet according to claim 1 .
10. A coated metal sheet comprising:
a metal sheet,
an intercoat coating film disposed on the metal sheet, and
an overcoat coating film disposed on the intercoat coating film,
wherein the overcoat coating film comprises a resin, a gloss adjusting agent which is particles having micropores, and a matting agent which is primary particles,
wherein a content of the gloss adjusting agent in the overcoat coating film is from 0.01 to 15 vol %,
wherein a content of the matting agent in the overcoat coating film is from 0.01 to 15 vol %, and
wherein the coated metal sheet satisfies the following equations:
D 1 97.5 /T≤ 0.7
Ru≤ 1.2 T
R≥ 1.0
5.0≤ D 2 97.5 /T≤ 7.0
3≤ T≤ 20
wherein R (μm) is a number average particle diameter of the gloss adjusting agent, T (μm) is a film thickness of the overcoat coating film, D1 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the gloss adjusting agent based on the number of particles, D2 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the matting agent based on the number of particles, and Ru (μm) is an upper limit particle diameter in a number particle size distribution of the gloss adjusting agent.
11. The coated metal sheet according to claim 10 , further comprising an undercoat coating film between the metal sheet and the intercoat coating film.
12. The coated metal sheet according to claim 10 , wherein the Ru is less than T.
13. The coated metal sheet according to claim 10 , wherein the metal sheet has been subjected to non-chromate anti-rust treatment, and the coated metal sheet is chromate-free.
14. The coated metal sheet according to claim 10 , wherein the metal sheet has been subjected to chromate anti-rust treatment.
15. The coated metal sheet according to claim 10 , wherein the gloss adjusting agent is silica particles.
16. The coated metal sheet according to claim 10 , having a glossiness at 75° is 1 to 25.
17. The coated metal sheet according to claim 10 , being a coated metal sheet for exterior use.
18. An exterior building material composed of the coated metal sheet according to claim 10 .
19. A method for producing a coated metal sheet comprising a metal sheet and an overcoat coating film to be disposed on the metal sheet, comprising the steps of:
applying an overcoat coating material containing a resin, a gloss adjusting agent, and a matting agent onto the metal sheet; and
curing the coating film of the overcoat coating material to form the overcoat coating film;
wherein a content of the gloss adjusting agent in the overcoat coating film is from 0.2 to 15 vol %, and a content of the matting agent in the overcoat coating film is from 0.2 to 15 vol %,
wherein the gloss adjusting agent is particles having micropores, and the matting agent is primary particles, and
wherein the gloss adjusting agent and the matting agent which satisfy the following equations are employed:
D 1 97.5 /T≤ 0.7
Ru≤ 1.2 T
R≥ 1.0
2.0≤ D 2 97.5 /T≤ 7.0
13≤ T≤ 20
wherein R (μm) is a number average particle diameter of the gloss adjusting agent, T (μm) is a film thickness of the overcoat coating film, D1 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the gloss adjusting agent based on the number of particles, D2 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the matting agent based on the number of particles, and Ru (μm) is an upper limit particle diameter in a number particle size distribution of the gloss adjusting agent.
20. The method for producing a coated metal sheet according to claim 19 , wherein the overcoat coating material has been subjected to treatment for pulverizing the particles in the overcoat coating material.
21. A method for producing a coated metal sheet comprising a metal sheet and an overcoat coating film to be disposed on the metal sheet, comprising the steps of:
applying an overcoat coating material containing a resin, a gloss adjusting agent, and a matting agent onto the metal sheet; and
curing the coating film of the overcoat coating material to form the overcoat coating film;
wherein a content of the gloss adjusting agent in the overcoat coating film is from 0.01 to 15 vol %, and a content of the matting agent in the overcoat coating film is from 0.01 to 15 vol %,
wherein the gloss adjusting agent is particles having micropores, and the matting agent is primary particles, and
wherein the gloss adjusting agent and the matting agent which satisfy the following equations are employed:
D 1 97.5 /T≤ 0.7
Ru≤ 1.2 T
R≥ 1.0
5.0≤ D 2 97.5 /T≤ 7.0
3≤ T≤ 20
wherein R (μm) is a number average particle diameter of the gloss adjusting agent, T (μm) is a film thickness of the overcoat coating film, D1 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the gloss adjusting agent based on the number of particles, D2 97.5 (μm) is a 97.5% particle diameter in an accumulated particle size distribution of the matting agent based on the number of particles, and Ru (μm) is an upper limit particle diameter in a number particle size distribution of the gloss adjusting agent.
22. The method for producing a coated metal sheet according to claim 21 , wherein the overcoat coating material has been subjected to treatment for pulverizing the particles in the overcoat coating material.