Glass composition for glass fiber
Provided is a glass composition for glass fiber allowing spinning to be stably performed without mixing of red foreign substances into glass fibers. The glass composition for glass fiber includes, in relation to the total amount thereof, SiO 2 in a content falling within a range from 57.0 to 60.0% by mass, Al 2 O 3 in a content falling within a range from 17.5 to 20.0% by mass, MgO in a content falling within a range from 8.5 to 12.0% by mass, CaO in a content falling within a range from 10.0 to 13.0% by mass and B 2 O 3 in a content falling within a range from 0.5 to 1.5% by mass, the total content of SiO 2 , Al 2 O 3 , MgO and CaO being 98.0% by mass or more.
1. A glass composition for glass fiber comprising, in relation to the total amount thereof, SiO 2 in a range of 57.0 to 60.0% by mass, Al 2 O 3 in a range of 17.5 to 20.0% by mass, MgO in a range of 8.5 to 12.0% by mass, CaO in a range of 10.0 to 13.0% by mass and B 2 O 3 in a range of 0.5 to 1.5% by mass, the total content of SiO 2 , Al 2 O 3 , MgO and CaO being 98.0% by mass or more.
2. The glass composition for glass fiber according to claim 1 , comprising, in relation to the total amount thereof, SiO 2 in a range of 57.5 to 59.5% by mass, Al 2 O 3 in a range of 18.0 to 19.5% by mass, MgO in a range of 8.8 to 11.5% by mass and CaO in a range of 10.3 to 12.5% by mass.
3. The glass composition for glass fiber according to claim 1 , comprising, in relation to the total amount thereof, SiO 2 in a range of 58.0 to 59.3% by mass, Al 2 O 3 in a range of 18.2 to 19.0% by mass, MgO in a range of 9.0 to 11.0% by mass and CaO in a range of 10.5 to 12.0% by mass.
4. The glass composition for glass fiber according to claim 1 , comprising, in relation to the total amount thereof, SiO 2 in a range of 58.0 to 59.3% by mass, Al 2 O 3 in a range of 18.2 to 19.0% by mass, MgO in a range of 9.0 to 11.0% by mass and CaO in a range of 10.5 to 11.9% by mass.
5. The glass composition for glass fiber according to claim 1 , wherein the ratio (CaO (% by mass)/Al 2 O 3 (% by mass)) of the content of CaO (% by mass) to the content of Al 2 O 3 (% by mass) is in a range of 0.50 to 0.72, and the ratio ((B 2 O 3 (% by mass)×CaO (% by mass))/Al 2 O 3 (% by mass)) of the product of the content of B 2 O 3 (% by mass) and the content (% by mass) of CaO to the content (% by mass) of Al 2 O 3 is in a range of 0.22 to 1.00.
6. The glass composition for glass fiber according to claim 1 , wherein the glass fibers produced from the glass composition for glass fiber comprises Cr 2 O 3 in a range of 0.001 to 0.010% by mass.
7. The glass composition for glass fiber according to claim 1 , wherein the fiber modulus of elasticity of the glass fibers produced from the glass composition for glass fiber is 83 GPa or more.
8. The glass composition for glass fiber according to claim 1 , wherein the linear expansion coefficient of the glass fibers produced from the glass composition for glass fiber in a temperature range of 50 to 200° C. is 4.2 ppm/K or less.
9. The glass composition for glass fiber according to claim 1 , wherein the fiber strength of the glass fibers produced from the glass composition for glass fiber is 4.0 GPa or more.
10. Glass fibers formed from a glass composition for glass fiber comprising, in relation to the total amount thereof, SiO 2 in a range of 57.0 to 60.0% by mass, Al 2 O 3 in a range of 17.5 to 20.0% by mass, MgO in a range of 8.5 to 12.0% by mass, CaO in a range of 10.0 to 13.0% by mass and B 2 O 3 in a range of 0.5 to 1.5% by mass, the total content of SiO 2 , Al 2 O 3 , MgO and CaO being 98.0% by mass or more,
wherein the glass fibers have non-circular cross sections each having the ratio (major axis/minor axis) of the major axis to the minor axis of the cross sectional shape in a range of 2.0 to 6.0 and the fiber diameter defined as the diameter of the perfect circle having the same area as the actual cross-sectional area of the fiber in a range of 10 to 30 μm.
11. Glass fibers formed from a glass composition for glass fiber comprising, in relation to the total amount thereof, SiO 2 in a range of 57.0 to 60.0% by mass, Al 2 O 3 in a range of 17.5 to 20.0% by mass, MgO in a range of 8.5 to 12.0% by mass, CaO in a range of 10.0 to 13.0% by mass and B 2 O 3 in a range of 0.5 to 1.5% by mass, the total content of SiO 2 , Al 2 O 3 , MgO and CaO being 98.0% by mass or more,
wherein the glass fibers have perfect circular cross sections and fiber diameters in a range of 3 μm or more and less than 10 μm.