ADHESIVE FILM AND PROCESS FOR PRODUCING THE SAME
The present invention provides an adhesive film hardly suffering from fisheyes and having excellent mechanical strength and heat resistance as well as good adhesion properties, which can be suitably used as various surface protective films, etc. The present invention relates to an adhesive film comprising a polyester film and an adhesive layer formed on at least one surface of the polyester film, in which the adhesive layer comprises a (meth)acrylic resin comprising a (meth)acrylate unit that comprises an alkyl group having not less than 4 carbon atoms at an ester end thereof, a content of the (meth)acrylate unit in the (meth)acrylic resin being not less than 20% by weight; and an adhesion strength to a polymethyl methacrylate plate of the adhesive layer is not less than 1 mN/cm.
1 . An adhesive film comprising a polyester film and an adhesive layer formed on at least one surface of the polyester film,
the adhesive layer comprising a (meth)acrylic resin comprising a (meth)acrylate unit that comprises an alkyl group having not less than 4 carbon atoms at an ester end thereof, a content of the (meth)acrylate unit in the (meth)acrylic resin being not less than 20% by weight; and an adhesion strength of the adhesive layer to a polymethyl methacrylate plate being not less than 1 mN/cm.
2 . The adhesive film according to claim 1 , wherein the adhesive layer has a thickness of not more than 10 μm.
3 . The adhesive film according to claim 1 , wherein the (meth)acrylic resin has a glass transition point of not higher than 0° C.
4 . The adhesive film according to claim 1 , wherein the (meth)acrylic resin is a compound having not more than 2 carbon atoms at an ester end thereof or a compound having a ring structure.
5 . The adhesive film according to claim 1 , wherein a content of a constitutional unit derived from the compound having not more than 2 carbon atoms at an ester end thereof in the (meth)acrylic resin is not more than 50% by weight.
6 . The adhesive film according to claim 1 , wherein a content of a constitutional unit derived from the compound having a ring structure in the (meth)acrylic resin is not more than 50% by weight.
7 . The adhesive film according to claim 1 , wherein the adhesive layer comprises a crosslinking agent.
8 . The adhesive film according to claim 1 , wherein a content of the crosslinking agent in the adhesive layer is not more than 60% by weight.
9 . The adhesive film according to claim 1 , wherein an arithmetic average roughness (Sa) of a surface of the adhesive layer is not more than 50 nm.
10 . The adhesive film according to claim 1 , further comprising a functional layer formed on a surface of the polyester film which is opposite to the surface provided with the adhesive layer.
11 . The adhesive film according to claim 1 , wherein a haze of the adhesive film is not more than 5.0%.
12 . A process for producing an adhesive film, comprising the steps of:
providing a coating layer on at least one surface of a polyester film, the coating layer comprising a (meth)acrylic resin comprising a (meth)acrylate unit that comprises an alkyl group having not less than 4 carbon atoms at an ester end thereof, a content of the (meth)acrylate unit in the (meth)acrylic resin being not less than 20% by weight; and
drawing the polyester film provided with the coating layer in at least one direction thereof.
13 . The process for producing an adhesive film according to claim 12 , wherein the adhesive layer has a thickness of not more than 10 μm.
14 . The process for producing an adhesive film according to claim 12 , wherein the (meth)acrylic resin has a glass transition point of not higher than 0° C.
15 . The process for producing an adhesive film according to claim 12 , wherein the (meth)acrylic resin is a compound having not more than 2 carbon atoms at an ester end thereof or a compound having a ring structure.
16 . The process for producing an adhesive film according to claim 12 , wherein a content of a constitutional unit derived from the compound having not more than 2 carbon atoms at an ester end thereof in the (meth)acrylic resin is not more than 50% by weight.
17 . The process for producing an adhesive film according to claim 12 , wherein a content of a constitutional unit derived from the compound having a ring structure in the (meth)acrylic resin is not more than 50% by weight.
18 . The process for producing an adhesive film according to claim 12 , wherein the adhesive layer comprises a crosslinking agent.
19 . The process for producing an adhesive film according to claim 12 , wherein a content of the crosslinking agent in the adhesive layer is not more than 60% by weight.
20 . The process for producing an adhesive film according to claim 12 , wherein an arithmetic average roughness (Sa) of a surface of the adhesive layer is not more than 50 nm.
21 . The process for producing an adhesive film according to claim 12 , wherein the adhesive film further comprises a functional layer formed on a surface of the polyester film which is opposite to the surface provided with the adhesive layer.
22 . The process for producing an adhesive film according to claim 12 , wherein a haze of the adhesive film is not more than 5.0%.