Colored translucent zirconia sintered body and powder, and application thereof
A zirconia sintered body is provided having a color tone equivalent to the color tone guides of various natural teeth and having the same aesthetics as a natural front tooth. The present invention provides a colored translucent zirconia sintered body comprising zirconia containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe 2 O 3 , less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.
1. A colored translucent zirconia sintered body comprising zirconia containing greater than 4.0mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 2,000 ppm of iron oxide in terms of Fe 2 O 3 , less than 0.01 wt. % of cobalt oxide in terms of CoO, and less than 0.1 wt. % of alumina; the zirconia sintered body having a relative density of not less than 99.90%, a total light transmittance of not less than 25% and less than 40% for light having a wavelength of 600 nm at a sample thickness of 1.0 mm, and a strength of not less than 500 MPa.
2. The colored translucent zirconia sintered body according to claim 1 , wherein an average crystal grain size is from 0.3 to 5.0 μm.
3. The colored translucent zirconia sintered body according to claim 1 , wherein a luminosity L* in an L*a*b color system is not less than 43 and not greater than 60.
4. The colored translucent zirconia sintered body according to claim 1 , wherein a monoclinic phase transformation depth after being immersed for 24 hours in hot water at 140° C. is not greater than 5 μm.
5. The colored translucent zirconia sintered body according to claim 1 , wherein a monoclinic phase ratio after being immersed for 72 hours in hot water at 140° C. is not greater than 5%.
6. The colored translucent zirconia sintered body according to claim 1 , wherein a crystal phase contains tetragonal and cubic phases.
7. A production method for the colored translucent zirconia sintered body according to claim 1 comprising:
a molding step of obtaining a green body by molding a zirconia powder composition containing greater than 4.0 mol % and not greater than 6.5 mol % of yttria, less than 0.25 mol % of erbia, less than 0.1 wt. % of an aluminum compound in terms of Al 2 O 3 , less than 2,000 ppm of iron compound in terms of Fe 2 O 3 , and less than 0.01 wt. % of cobalt compound in terms of CoO; and a sintering step of sintering the green body under normal pressure at 1,400 to 1,600° C.
8. The production method according to claim 7 , wherein the zirconia powder composition contains at least two types selected from the group consisting of: a zirconia mixed powder containing greater than 0 wt. % and less than 0.09 wt .% of an aluminum compound, the remainder being zirconia stabilized with greater than 4 mol % and not greater than 6.5 mol % of yttria; a zirconia mixed powder containing greater than 0 wt. % and less than 0.09 wt. % of an aluminum compound in terms of Al 2 O 3 and not less than 2,000 ppm and not greater than 3,000 ppm of an iron compound in terms of Fe 2 O 3 , the remainder being zirconia stabilized with greater than 4 mol % and not greater than 6.5 mol % of yttria; a zirconia mixed powder containing greater than 0 wt. % and less than 0.09 wt. % of an aluminum compound in terms of Al 2 O 3 and not less than 0.03 wt. % and not greater than 0.05 wt. % of a cobalt compound in terms of CoO, the remainder being zirconia stabilized with greater than 4 mol % and not greater than 6.5 mol % of yttria; and a zirconia mixed powder containing greater than 0 wt. % and less than 0.09 wt. % of an aluminum compound in terms of Al 2 O 3 , the remainder being zirconia stabilized with greater than 2 mol % and not greater than 5 mol % of erbia.
9. The production method according to claim 7 , wherein the iron compound is at least one selected from the group consisting of iron oxide hydroxide and iron oxide.
10. The production method according to claim 7 , wherein the aluminum compound is alumina.
11. A dental material comprising the colored translucent zirconia sintered body according to claim 1 .