Sinterable feedstock for use in 3D printing devices

1. A filament suitable to be used in a 3D printing device, wherein the filament comprises

(a) a metal and/or ceramic powder;

(b) a thermoplastic binder comprising a thermoplastic polymer and at least one plasticizer; and

(c) between 0 and 10 wt % of additives based on the total weight of the filament

and wherein the filament has a Shore A hardness of at least 85 at 20° C. and

wherein the at least one plasticizer is a mixture of esters and wherein the mixture of esters comprises an ester which is solid at 20° C. and an ester that is liquid at 20° C.

2. The filament according to claim 1 , wherein the metal and/or ceramic powder is sinterable.

3. The filament according to claim 1 , wherein the thermoplastic polymer is selected from the group consisting of a polyurethane, a polyamide, a polyvinylpyrrolidon, a polyacrylate, a polyolefin and a mixture thereof.

4. The filament according to claim 3 , wherein the polyamide is selected from the group consisting of a copolyamide, Polyamide 11, Polyamide 12, a polyether-blockamide and mixtures thereof.

5. The filament according to claim 1 , wherein the plasticizer is removable at least in part from the filament by extraction at a temperature of at least 20° C. using an organic solvent.

6. The filament according to claim 1 , wherein the at least one plasticizer is a substituted or non-substituted aromatic or heteroaromatic carboxylic acid ester or mixtures thereof.

7. The filament according to claim 1 , wherein said at least one plasticizer is a mixture of hydroxybenzoic acid esters.

8. The filament according to claim 7 , wherein the hydroxybenzoic acid esters are esters of hydroxybenzoic acid and a branched or linear alcohol, wherein the alcohol is selected from the group consisting of a branched or linear C8-C22 alcohol and mixtures thereof and preferably selected from 2-propyl heptyl alcohol, isodecyl alcohol, 1-docosanol, 1-octadecanol, 1-dodecanol, 2-ethylhexyl alcohol and mixtures thereof.

9. The filament according to claim 7 , wherein the hydroxybenzoic acid esters is a p-hydroxybenzoic acid ester.

10. The filament according to claim 1 , wherein the thermoplastic binder comprises between 40 wt % and 70 wt % of plasticizer based on the total weight of the binder.

11. The filament according to claim 1 , wherein the thermoplastic binder has a melting temperature of between 100° C. and 190° C.

12. The filament according to claim 1 , wherein the filament is elastic, has a diameter of between 0.5 mm and 5 mm and a length of at least 10 cm.

13. The filament according to claim 1 , comprising

(a) from 80 to 95 wt % based on the total weight of the filament of the metal and/or ceramic powder,

(b) from 2 to 8 wt % based on the total weight of the filament of the thermoplastic polymer and from 1 to 5 wt % based on the total weight of the filament of plasticizer, and

(c) from 0 to 1 wt % based on the total weight of the filament of the additives wherein the sum of the listed ingredients is 100 wt %, based on the total weight of the filament.

14. A process for producing a shaped body, the process comprising the following steps: (i) printing a shaped green body using the filament according to claim 1 and a 3D-printing device; (ii) removing at least part of the plasticizer from the shaped green body; and (iii) sintering the shaped green body obtained from step (ii) to obtain said shaped body.

15. The process according to claim 14 , wherein in step (ii) the plasticizer is extracted by contacting the green body with an organic solvent capable of extracting the plasticizer wherein said extraction does not change the shape of the shaped green body.

16. The filament according to claim 1 , wherein the Shore A hardness is measured in accordance to DIN ISO 7619-1 standard using a HPE II hardness tester.