BIODEGRADABLE REINFORCED PAPER PACKAGING MATERIAL AND ITS MANUFACTURING METHOD
A paper packaging material, and method for manufacturing it, having a paper layer with a polyethylene coating on one surface, a biodegradable resin grid on the opposite surface to enhance its strength while maintaining reduced weight and a thermo-sealing resin, which eliminates the use of glues in the packaging process. The vegetal resin is made out of vegetable wax, acrylic styrene copolymer, demineralized water, water based silicone and natural fungicide. The method includes the steps of printing graphics on one side of the web, drying the paper, applying a vegetal resin on the other side and a film of polyethylene on the top of the printed side. Thermo-sealing varnish is applied in predetermined areas.
1 . A packaging material, comprising:
A) a paper web having between 70 and 85 gsm having first and second surfaces;
B) a layer of biodegradable vegetal resin covering said first surface, said layer having a thickness between 3 and 4 gsm and further including said vegetal resin engraved on said first surface;
C) a polyethylene film covering said second surface, said film having a thickness between 8 and 10 msg; and
D) an effective amount of a thermo-sealing varnish applied on selected areas over the polyethylene film and cooperatively selected for predetermined applications of the packaging material.
2 . The packaging material set forth in claim 1 wherein said resin consists essentially of a vegetal wax, acrylic styrene copolymer, demineralized water, water based silicone and a natural fungicide.
3 . The packaging material set forth in claim 2 wherein said resin consists essentially of: acrylic styrene copolymer between 23% and 33% of the weight of said resin, vegetable wax between 45% and 55% of the weight of said resin, demineralized water between 15% and 22% of the weight of said resin, and water based silicone between 0.8% and 1.2% of the weight of said resin.
4 . A method for manufacturing a package material, comprising the steps of:
A) printing graphics on one of the surfaces of a paper web;
B) drying the paper web by removing between 30 to 60 percent of its moisture;
C) applying a vegetal resin uniformly on the other surface of said paper web and engraving thereon an alveolar shaped design that penetrates said dried paper, said vegetal resin consisting essentially of vegetal wax, acrylic styrene copolymer demineralized water, water based silicone and a biocidal element so that said other surface is mechanically reinforced and its impermeability increased;
D) applying a layer of polyethylene on said one surface on top of the printed graphics in said first step; and
E) applying a thermo sealing varnish in predetermined areas that will cooperate to the use of the paper package material for predetermined application.
5 . The method set forth in claim wherein said vegetal resin consists essentially of: acrylic styrene copolymer between 23% and 33% of the weight of said resin, vegetable wax between 45% and 55% of the weight of said resin, demineralized water between 15% and 22% of the weight of said resin, and water based silicone between 0.8% and 1.2% of the weight of said resin.
6 . The method set forth in claim 5 wherein said paper web has a thickness between 70 and 85 gsm, and said vegetal resin layer has a thickness between 3 and 4 msg.