Assembly and mounting of solar cells on airfoils
A method of fabricating a solar cell array on the surface of a support by providing an assembly fixture having a smooth, concave surface; mounting a film composed of ethylene tetrafluoroethylene (ETFE) directly on the surface of the fixture; mounting a film composed of a non-crosslinked silicone pressure sensitive adhesive directly over the ETFE film; mounting an array of interconnected solar cells directly over the adhesive film. An uncured supporting film composed of a composite material is mounted directly on the back side of the solar cells; and the film of composite material is co-cured so that the array of interconnected solar cells is bonded to the supporting film. The bonded and cured film of composite material and an array of interconnected solar cells with the ETFE film is then removed from the assembly fixture.
1. A method of fabricating a solar cell array on the surface of a support comprising:
providing an assembly fixture having a smooth, concave surface;
mounting a film composed of ethylene tetrafluoroethylene (ETFE) directly on the surface of the fixture;
mounting a film composed of a non-crosslinked silicone pressure sensitive adhesive directly over the ETFE film;
mounting an array of interconnected solar cells having a front (light receiving) side and a back side, directly over the adhesive film;
mounting an uncured supporting film composed of a composite material directly on the back side of the solar cells;
co-curing the film of composite material so that the array of interconnected solar cells is bonded to the supporting film; and
removing the bonded and cured film of composite material and an array of interconnected solar cells with the ETFE film from the assembly fixture.
2. A method as defined in claim 1 , wherein the pressure sensitive adhesive film is between 0.001 and 0.010 inches in thickness.
3. A method as defined in claim 1 , wherein the array of solar cells is between 0.010 and 0.030 inches in thickness.
4. A method as defined in claim 1 , wherein the film of composite material is between 0.001 and 0.020 inches in thickness.
5. A method as defined in claim 1 , wherein the film of composite material is composed of a para-aramid fabric.
6. A method as defined in claim 5 , further comprising a foam supporting structure bonded to the film of the composite material.
7. A method as defined in claim 1 , wherein the film of composite material is composed of a poly (4, 4′-oxydiphenylene-pyromellitimide) material.
8. A method as defined in claim 1 , wherein the array of interconnected solar cells are III-V compound semiconductor multijunction solar cells.
9. A method as defined in claim 1 , wherein the concave surface of the assembly fixture has a surface roughness of less than 0.001 inches rms.
10. A method as defined in claim 9 , wherein the concave surface of the assembly fixture forms an airfoil shaped surface.
11. A method as defined in claim 1 , wherein the pressure sensitive adhesive is a single monomer or co-monomer silicone blend.