Phosphor, fabricating method thereof, method for regulating crystal phase thereof, and method for changing crystal phase hereof
View Patent ↗The present disclosure provides a method for fabricating a phosphor. A first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 4 in a hydrofluoric acid solution. An anhydrous ethanol is added to the first solution to make a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 equal to or less than 48M to form a precipitate. Afterward, the precipitate is collected.
1. A method for fabricating a phosphor, comprising:
(a) providing a first solution, wherein the first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 4 in a hydrofluoric acid solution;
(b) adding an anhydrous ethanol to the first solution to make a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 equal to or less than 48M to form a precipitate; and
(c) collecting the precipitate after step (b).
2. The method for fabricating the phosphor as claimed in claim 1 , wherein step (a) and step (b) are performed at room temperature.
3. The method for fabricating the phosphor as claimed in claim 1 , wherein the phosphor emits a red light having a peak wavelength in a range of about 600 nm to about 650 nm after being excited by a light having a peak wavelength in a range of about 320 nm to about 500 nm.
4. The method for fabricating the phosphor as claimed in claim 1 , wherein the phosphor has a particle size in a range of about 0.3 μm to about 30 μm.
5. The method for fabricating the phosphor as claimed in claim 1 , wherein the total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 in step (b) is in a range of about 23M to 48M.
6. The method for fabricating the phosphor as claimed in claim 5 , wherein the phosphor has a particle size in a range of about 10 μm to about 30 μm.
7. A method for fabricating a phosphor, comprising:
(a) providing a first solution, wherein the first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 4 in a hydrofluoric acid solution;
(b) adding an anhydrous ethanol to the first solution to make a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 equal to or less than 16M to form a precipitate; and
(c) collecting the precipitate after step (b).
8. The method for fabricating the phosphor as claimed in claim 7 , wherein step (a) and step (b) are performed at room temperature.
9. The method for fabricating the phosphor as claimed in claim 7 , wherein the phosphor emits a red light having a peak wavelength in a range of about 600 nm to about 650 nm after being excited by a light having a peak wavelength in a range of about 320 nm to about 500 nm.
10. The method for fabricating the phosphor as claimed in claim 7 , wherein the phosphor shows a zero phonon line (ZPL) having a peak wavelength in a range of about 620 nm to about 625 nm.
11. The method for fabricating the phosphor as claimed in claim 7 , wherein the phosphor has a particle size in a range of about 0.3 μm to about 1 μm.
12. A phosphor represented by the following formula:
K 2 [Ge 1-x F 6 ]:Mn x 4+ , wherein 0< x< 0.2,
wherein the phosphor has a hexagonal phase with a P6 3 mc space group, and the phosphor is fabricated by the method as claimed in claim 7 ;
wherein the phosphor has a particle size in a range of about 0.3 μm to about 1 μm.
13. A method for regulating a crystal phase of a phosphor, comprising:
(a) providing a first solution, wherein the first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 1 in a hydrofluoric acid solution; and
(b) adding an anhydrous ethanol to the first solution to regulate a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 to control the crystal phase of a resulting precipitate;
wherein step (b) comprises regulating the total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 to be in a range of about 23M to 48M to make the phosphor have a hexagonal phase with a P 3 m1 space group.
14. A method for regulating a crystal phase of a phosphor, comprising:
(a) providing a first solution, wherein the first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 4 in a hydrofluoric acid solution; and
(b) adding an anhydrous ethanol to the first solution to regulate a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 to control the crystal phase of a resulting precipitate;
wherein step (b) comprises regulating the total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 equal to or less than 16M to make the phosphor have a hexagonal phase with a P6 3 mc space group.
15. A method for changing a crystal phase of a phosphor, comprising:
(a) providing a first solution, wherein the first solution is formed by dissolving potassium hexafluorogermanate (K 2 GeF 6 ) and either K 2 MnF 6 or KMnO 4 in a hydrofluoric acid solution; and
(b) adding an anhydrous ethanol to the first solution to make a total concentration of fluoride ions of potassium hexafluorogermanate (K 2 GeF 6 ), hydrofluoric acid, and either K 2 MnF 6 or KMnO 4 be in a range of about 16M to about 23M to change the crystal phase of a resulting precipitate;
wherein the change of the crystal phase comprises a change between a hexagonal phase with a P 3 m1 space group and a hexagonal phase with a P6 3 mc space group.