Particles for monolithic refractory
Particles for a monolithic refractory are made of a spinet porous sintered body which is represented by a chemical formula of MgAl 2 O 4 , wherein pores having a pore size of 0.01 μm or more and less than 0.8 μm occupy 10 vol % or more and 50 vol % or less with respect to a total volume of pores having a pore size of 10 μm or less in the particles, and the particles for a monolithic refractory have grain size distribution in which particles having a particle size of less than 45 μm occupy 60 vol % or less, particles having a particle size of 45 μm or more and less than 100 μm occupy 20 vol % or more and 60 vol % or less, and particles having a particle size of 100 μm or more and 1000 μm or less occupy 10 vol % or more and 50 vol % or less.
1. Particles for a monolithic refractory, said particles comprising spinel porous sintered bodies represented by a chemical formula of MgAl 2 O 4 ,
wherein pores having a pore size of 0.01 μm to less than 0.8 μm occupy 10 vol % to 50 vol % with respect to a total volume of pores having a pore size of 10 μm or less in the particles for a monolithic refractory, and
the particles for a monolithic refractory have grain size distribution in which particles having a particle size of less than 45 μm occupy 60 vol % or less, particles having a particle size of 45 μm to less than 100 μm occupy 20 vol % to 60 vol %, and particles having a particle size of 100 μm to 1000 μm occupy 10 vol % to or more and 50 vol %.