Cotton performance products and methods of their manufacture
Performance fabrics and methods of manufacturing them where the fabric is knit or woven cotton and cotton elastane blends to which a moisture-management treatment of wax or wax emulsion is applied to one side of the woven or knitted fabric. The treated fabric is wicking, absorbent and not water repellant or water resistant.
1. A moisture management treated fabric comprising:
a fabric of knit or woven fibers or yarns comprising cotton; and
a treatment applied to the fabric, the treatment consisting essentially of a dendrimer wax solution, suspension or emulsion, said treatment applied to the fabric is continuous, the amount of the treatment on the fabric is 0.5% to 5% by weight solids add on after the treated fabric is dried,
wherein the treated fabric has a drying rate faster than that of untreated fabric when using a heated plate apparatus.
2. The fabric of claim 1 , wherein the treatment is applied to one side of the fabric.
3. The fabric of claim 1 , wherein the fabric is constructed into a garment.
4. The fabric of claim 3 , wherein the treatment is applied to the side of the garment that will be adjacent to a wearer's skin.
5. The fabric of claim 1 , wherein the amount of treatment on the fabric is 1% to about 3.5% by weight solids add on the treatment is dried.
6. The fabric of claim 1 , wherein the amount of treatment on the fabric is 2% to about 3% by weight solids add on after the treatment is dried.
7. The fabric of claim 1 , wherein the knit or woven fibers or yarns comprise at least 50% by weight cotton.
8. The fabric of claim 1 , wherein the knit or woven fibers or yarns comprise at least 75% by weight cotton.
9. The fabric of claim 1 , wherein the knit or woven fibers or yarns comprise at least 90% by weight cotton.
10. The fabric of claim 1 , wherein the knit or woven fibers or yarns consist of cotton.
11. The fabric of claim 1 , wherein the knit or woven fibers or yarns are a cotton elastane blend.
12. The fabric of claim 1 , further comprising at least one metal having a +1 or +2 charge.
13. The fabric of claim 12 , comprising at least one of reactive copper and reactive zinc.
14. The fabric of claim 1 , wherein the fabric has a vertical wick that is greater than that of untreated fabric.
15. A moisture management fabric comprising:
a fabric of knit or woven fibers or yarns comprising cotton; and
0.05% to 5% by weight dendrimer wax applied on the fabric, wherein the fabric has a drying rate faster than that of untreated fabric, said drying rate measured using a heated plate apparatus.
16. A moisture management treated fabric comprising:
a fabric of knit or woven fibers or yarns comprising cotton; and
a continuous wax treatment comprising dendrimer wax in a solvent or diluent applied to the fabric, wherein the fabric contains 0.5% to 5% by weight add on dendrimer wax after the treated fabric is dried, wherein the treated fabric has a drying rate faster than that of untreated fabric when using a heated plate apparatus.
17. A method of manufacturing the treated fabric of claim 1 comprising:
spraying a wax solution or a wax emulsion on a knitted or woven fabric comprising cotton;
heating the fabric sprayed with the wax solution or wax emulsion to 167° C. for at least 10 seconds.
18. The method of claim 17 , further comprising the steps of spraying at least one water soluble copper or zinc salt or complex on the fabric and heating the fabric sprayed with the at least one water soluble copper or zinc salt or complex to between 135° C. to 140° C. for at least 10 seconds.
19. The method of claim 18 , wherein the steps of spraying at least one water soluble copper or zinc salt or complex on the fabric and heating the fabric to between 135° C. to 140° C. for at least 10 seconds occur before the step of spraying the wax or wax emulsion.