Barrier film for food packaging
Barrier films are prepared from a blend of two high density polyethylene blend components and a high performance organic nucleating agent. The two high density polyethylene blend components have substantially different melt indices. Large reductions in the moisture vapor transmission rate of the film are observed in the presence of the nucleating agent when the melt indices of the two blend components have a ratio of greater than 10/1. The resulting barrier films are suitable for the preparation of packaging for dry foods such as crackers and breakfast cereals.
1. A polyethylene film comprising at least one layer, wherein said layer is prepared from a mixture comprising;
a) from about 5 to about 60 weight percent, based on the total weight of said mixture, of a component a) comprising at least one high density polyethylene having a density of from 0.950 to 0.975 g/cc and a high melt index I 2 ;
b) from about 95 to about 40 weight percent, based on the total weight of said mixture, of a component b) comprising at least one high density polyethylene having a density from about 0.950 to about 0.970 g/cc and a low melt index I 2 ′, and;
c) from about 100 to about 3,000 ppm of a calcium salt of 1,2-cyclohexanedicarboxylic acid;
wherein, a melt index ratio, defined by dividing said high melt index I 2 of said component a) by said low melt index I 2 ′ of said component b), is greater than 10/1;
wherein the water vapor transmission rate of said polyethylene film is improved, by being from about 20% to about 53% lower, relative to a control polyethylene film of the same composition but not containing said calcium salt of 1,2-cyclohexanedicarboxylic acid;
wherein density is measured according to ASTM D 1505, and;
wherein melt index is measured according to ASTM D 1238 when conducted at 190° C. using a 2.16 kg weight.
2. The polyethylene film according to claim 1 , wherein said mixture has a density from about 0.955 to about 0.967 g/cc.
3. The polyethylene film according to claim 1 , wherein said mixture has a melt index, I 2 , from about 0.8 to about 8 grams/10 minutes.
4. The polyethylene film according to claim 1 , wherein said film is a multilayer film comprising at least one layer comprising said mixture.
5. A method for improving the barrier properties of a polyethylene film, said method comprising the steps of converting into a film a mixture comprising;
a) from about 5 to about 60 weight percent, based on the total weight of said mixture, of a component a) comprising at least one high density polyethylene having a density of from about 0.950 to about 0.975 g/cc and a high melt index I 2 ;
b) from about 95 to about 40 weight percent, based on the total weight of said mixture, of a component b) comprising at least one high density polyethylene having a density of from about 0.950 to about 0.970 g/cc and a low melt index I 2 ′, and;
c) from about 100 to about 3,000 ppm of a calcium salt of 1,2-cyclohexanedicarboxylic acid;
wherein, a melt index ratio, defined by dividing said high melt index I 2 of said component a) by said low melt index I 2 ′ of said component b), is greater than 10/1;
wherein the water vapor transmission rate of said polyethylene film is improved, by being from about 20% to about 53% lower, relative to a control polyethylene film of the same composition but not containing said calcium salt of 1,2-cyclohexanedicarboxylic acid;
wherein density is measured according to ASTM D 1505, and;
wherein melt index is measured according to ASTM D 1238 when conducted at 190° C. using a 2.16 kg weight.
6. The method of claim 5 , wherein said mixture has a density from about 0.955 to about 0.967 g/cc.
7. The method of claim 5 , wherein said mixture has a melt index, I 2 , from about 0.8 to about 8 grams/10 minutes.