Copper foil for producing graphene and method of producing graphene using the same
A copper foil for producing graphene, having 60 degree gloss of 500% or more in a rolling direction and a direction transverse to the rolling direction, and an average crystal grain size of 200 μm or more after heating at 1000° C. for 1 hour in an atmosphere containing 20% by volume or more of hydrogen and balance argon.
1. A rolled copper foil for producing graphene, having 60 degree gloss of 500% or more in a rolling direction and a direction transverse to the rolling direction, and an average crystal grain size of 200 μm or more after heating at 1000° C. for 1 hour in an atmosphere containing 20% by volume or more of hydrogen and balance argon.
2. The rolled copper foil for producing graphene according to claim 1 , wherein the average crystal grain size is 400 μm or more.
3. The rolled copper foil for producing graphene according to claim 1 , wherein the average crystal grain size is 900 μm or more.
4. The rolled copper foil for producing graphene according to claim 1 , wherein a superficial arithmetic mean roughness Ra is 0.05 μm or less.
5. A rolled copper foil for producing graphene, having an average crystal grain size of 200 μm or more after heating at 1000° C. for 1 hour in an atmosphere containing 20% by volume or more of hydrogen and balance argon, and wherein a superficial arithmetic mean roughness Ra is 0.05 μm or less.
6. The rolled copper foil for producing graphene according to claim 5 , wherein the superficial arithmetic mean roughness Ra is 0.03 μm or less.
7. The rolled copper foil for producing graphene according to claim 1 , prepared from a copper composition consisting of tough pitch copper in accordance with JIS-H3100-2000 or JIS-H3250-2000; consisting of oxygen free copper in accordance with JIS-H3100-2000 or JIS-H3510-1992; or consisting of a composition wherein 0.050% by mass or less of one or more elements selected from the group consisting of Sn and Ag is added to the tough pitch copper or the oxygen free copper.
8. A method of producing graphene using the rolled copper foil for producing graphene according to claim 1 , comprising the steps of:
heating the rolled copper foil for producing graphene while providing a carbon-containing gas to form graphene on a surface of the heated rolled copper foil; and
laminating a transfer sheet on the surface of the graphene, and etching and removing the rolled copper foil for producing graphene while transferring the graphene to the transfer sheet.
9. The rolled copper foil of according to claim 1 , having an oil film equivalent upon final rolling of 18000 or less.