Synergistic combinations of choline and reactive silanes in antimicrobial coatings
The invention relates to an antimicrobial coating composition formed by admixing choline bitartrate or choline chloride, an aminopropyltrialkoxysilane and water. This coating composition is preferably sprayed onto a surface and allowed to dry. Preferably the surface is a stainless steel surface. The coating reduces the amount of E. Coli on the surface of the substrate.
1. An antimicrobial coating, formed by a method comprising:
(a) providing a mixture consisting essentially of:
(i) 15 wt. % choline chloride;
(ii) 5 wt. % 3-aminopropyltriethoxysilane; and
(iii) remainder water;
(b) spraying said mixture onto a substrate surface; and
(c) allowing said mixture to nominally dry to form said antimicrobial coating on said substrate.
2. The antimicrobial coating of claim 1 , wherein said substrate is stainless steel.
3. The antimicrobial coating of claim 2 , wherein said antimicrobial coating exhibits about a 3.36 log reduction in E. Coli 25592 1 hour after initial inoculation of the coating with E. Coli 25592.
4. The antimicrobial coating of claim 2 , wherein said antimicrobial coating exhibits about a 6.60 log reduction in E. Coli 25592 4 hours after initial inoculation of the coating with E. Coli 25592.
5. An antimicrobial coating, formed by a method comprising:
(a) providing a mixture of:
(i) choline bitartrate;
(ii) 3-aminopropyltriethoxysilane; and
(iii) water;
(b) spraying said mixture onto a substrate surface; and
(c) allowing said mixture to nominally dry to form said antimicrobial coating on said substrate.
6. The antimicrobial coating of claim 5 , wherein said substrate is stainless steel.
7. The antimicrobial coating of claim 6 , wherein said antimicrobial coating exhibits about a log 3.38 reduction in E. Coli 25592 1 hour after initial inoculation of the coating with E. Coli 25592.
8. The antimicrobial coating of claim 6 , wherein said antimicrobial coating exhibits about a log 6.60 reduction in E. Coli 25592 4 hours after initial inoculation of the coating with E. Coli 25592.
9. The antimicrobial coating of claim 5 , wherein said mixture consists essentially of: (i) about 15% choline bitartrate; (ii) about 5% 3-aminopropyltriethoxysilane; and (iii) remainder water.