Method for treating reinforcing fibre and method for producing a reinforced composite article from the treated fibre

1. A molded composite material, comprising a cured reinforced composite material, wherein the cured reinforced composite material comprises at least one cured resin having:

i) a polymer having a monomer content of between about 5 to 30% w/w; and

ii) a plurality of reinforcing fibers coated with a coupling agent;

wherein:

a) the at least one cured resin adjacent to said reinforcing fibers defines an interphase; and,

b) the coated plurality of reinforcing fibers are treated such that the properties of said interphase are substantially equivalent to those of the bulk cured resin.

2. The molded composite material of claim 1 , wherein the polymer comprises between 5 to 50% w/w of the at least one cured resin.

3. The molded composite material of claim 1 , wherein the at least one cured resin has flexural toughness greater than about 3 Joules when tested in a standard flexure test, the test piece having dimensions about 100 mm in length, 15 mm in width and 5 mm in thickness.

4. The molded composite material of claim 1 , wherein the cured reinforced composite material has flexural toughness greater than 3 Joules for up to 5 years.

5. The molded composite material of claim 1 , wherein the treatment is a polymeric coating and/or a hydrophilic surface coating applied to said coated plurality of reinforcing fibers.

6. The molded composite material of claim 5 , wherein:

i) the polymer of said polymeric coating is an unsaturated polyester resin having less than about 30% w/w monomer; or

ii) the hydrophilic surface coating is prepared by reacting a vinyl functional silane with a polyol.

7. The molded composite material of claim 6 , wherein the unsaturated polyester resin is provided by reacting a polyol with an acid;

wherein:

i) the polyol comprises propylene glycol, methyl propanediol, neopentyl glycol, or diethyleneglycol;

ii) the acid comprises terephthalic acid, isophthalic acid, fumaric acid, or 1,4-cyclohexane diacid; and

iii) the unsaturated polyester resin comprises a saturated to unsaturated acid ratio of between about 1.2:1 to 2:1.

8. The molded composite material of claim 1 , wherein the coupling agent is a vinyl functional silane.

9. The molded composite material of claim 1 , wherein the coupling agent is selected from the group consisting of methacryloxypropyltrimethoxysilane, vinylbenzylaminoethylaminopropyl-trimethoxysilane, and vinyl-tris(acetoxy) silane.

10. The molded composite material of claim 1 , wherein the reinforcing fiber of the plurality of reinforcing fibers is a glass fiber.

11. The molded composite material of claim 10 , wherein the glass fiber has a length of between about 100 and 1000 microns.

12. The molded composite material of claim 1 , wherein the properties comprise:

i) mechanical properties selected from the group consisting of strength, toughness, and brittleness, or a combination thereof;

ii) physical or chemical properties selected from the group consisting of density, cross-link density, chemical resistance, molecular weight, and degree of crystallinity, or a combination thereof; or

iii) or a combination of the mechanical, physical, or chemical properties.

13. The molded composite material of claim 1 , wherein the cured composite material comprises one or more of the following:

i) a flexural modulus of greater than about 3.5 GPa;

ii) a flexural stress of greater than about 120 MPa; or

iii) an elongation at break of greater than about 2%.

14. The molded composite material of claim 1 , wherein the treatment:

i) reduces catalyzation of resin polymerization polymerization in the interphase when compared to a fiber not treated; or

ii) reduces embrittlement of said interphase when compared to a fiber not treated.