Building membrane with porous pressure sensitive adhesive

1. A process for making a water resistant, air permeable and vapor permeable membrane with a permeable pressure sensitive adhesive (PSA) backing comprising the steps of:

a) adding water in an amount ranging from about 40% to about 50% by weight to an acrylic copolymer pressure sensitive adhesive ranging from about 45% to about 50% by weight and mixing same to reduce the viscosity of the solution;

b) adding at least one solvent-free surfactant to the water copolymer solution and mixing same for a suitable time period to form air bubbles entrained throughout the copolymer pressure sensitive adhesive and surfactant solution;

c) pouring the bubble containing solution of adhesive and surfactant into a coater;

d) coating the bubble containing solution of adhesive and surfactant onto a water resistant vapor permeable polyester membrane to cover a surface of said membrane with a coating having thickness ranging from about 3 mils to about 5 mils;

e) heating the coated membrane at a suitable temperature for a suitable time to cure the pressure sensitive adhesive solution with the entrained bubbles to form interconnected pores in the now permeable coating; and

f) mounting a removable release cover to the coating over the cured pressure sensitive adhesive.

2. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 1 wherein said coating is heated at a temperature ranging from about 165° to about 265° F.

3. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 1 in step b) wherein said mixing is accomplished by a high speed dispersion mixer rotated at about 5000 rpm.

4. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 1 step b) wherein about 80% to about 90% of said formed air bubbles are sized from about 200 to about 300 microns.

5. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 1 wherein after step b) a fire retardant material is added to the copolymer surfactant mixture in the amount of about 2% to about 3% by weight.

6. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 1 wherein the coating of step d) is applied with a blade coater.

7. A process for making a water resistant, air permeable and vapor permeable membrane with a porous pressure sensitive adhesive (PSA) copolymer backing comprising the steps of:

a) adding water in an amount ranging from about 40% to about 50% by weight to a pressure sensitive adhesive copolymer having a backbone of n-butyl acrylate, 2-ethylhexyl acrylate, and vinyl acetate and mixing the water and pressure sensitive adhesive copolymer to form a solution;

b) adding a surfactant to said solution to provide for emulsification;

c) adding a second surfactant to said solution to provide a foaming agent;

d) adding a thickener to said solution of step c) and mixing the solution in a sheer mixer at a rate of speed for a suitable time to form and entrain air bubbles in said solution having a designated size range throughout the solution;

e) transferring the bubble containing solution into a coater feeder;

f) coating the adhesive surfactant thickener solution onto a water resistant vapor permeable spun polypropylene membrane to cover the surface of said membrane with said coating having a thickness ranging from about 3 mils to about 5 mils;

g) heating the coated membrane at a suitable temperature to accomplish curing of the adhesive surfactant thickener composite solution for a suitable time to cure said entrained air bubbles in place forming interconnected pores in the cured pressure sensitive adhesive; and

h) securing a removable release cover to the coated membrane pressure sensitive adhesive.

8. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 7 wherein a fire retardant material is added to the water copolymer surfactant solution after step c).

9. A process for making a water resistant air permeable and vapor permeable membrane with a porous pressure sensitive adhesive (PSA) backing comprising the steps of:

a) adding water in an amount ranging from about 40% to about 50% by weight to a pressure sensitive adhesive to form a water adhesive mixture, said pressure sensitive adhesive having a copolymer backbone of n-butyl acrylate, 2-ethylhexyl acrylate, and vinyl acetate and mixing said water adhesive mixture to form a uniform solution;

b) adding at least one surfactant to the uniform water copolymer solution and mixing same to form a pressure sensitive adhesive solution;

c) mixing said pressure sensitive adhesive solution for a suitable time in a sheer mixer forming air bubbles throughout the water, copolymer pressure sensitive adhesive and surfactant solution;

d) pouring the air bubble containing solution of water, copolymer pressure sensitive adhesive and surfactant into a coater assembly;

e) coating the bubble containing solution onto a water resistant vapor permeable polyester membrane to cover an outer surface of said membrane with a coating having a thickness which will entrain air bubbles ranging from about 200 microns to about 300 microns in size;

f) heating the coated membrane at a suitable temperature for a suitable time to cure the air bubbles in place in the bubble containing solution to form a cured pressure sensitive coating with interconnected pores positioned throughout the coating with some of said interconnected pores penetrating the surface of the coating to create a vapor permeable coating; and

g) mounting a removable release cover to the coated, membrane pressure sensitive adhesive.

10. A process for making a water resistant air permeable and vapor permeable membrane with a porous pressure sensitive adhesive copolymer coating as claimed in claim 9 wherein in step c) 80% to about 90% of said formed air bubbles are sized from about 200 to about 300 microns.

11. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said coated membrane is cured in step f) at a temperature ranging from about 165° F. to about 265° F.

12. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said at least one surfactant are two surfactants, one surfactant to provide emulsion and air bubble size and a second surfactant being a foaming agent.

13. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein in step c) said surfactant, water and copolymer pressure sensitive adhesive mixture solution is mixed in a sheer mixer to entrain air bubbles uniformly in said solution.

14. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said at least one surfactant includes a long chain alcohol which creates a stable emulsion.

15. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said coated membrane is cured in step f) at a temperature ranging from about 165° F. to about 265° F.

16. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 step c) wherein about 80% to about 90% of said formed air bubbles range in size from about 200 microns to about 300 microns.

17. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said formed pores are generally round and oval in shape and are evenly distributed throughout the adhesive coating and across the coating surface to form a vapor pathway through the adhesive coating.

18. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said mixing in step c) is undertaken by a high speed dispersion mixer mixed at about 5000 RPM for about 10 minutes to about 15 minutes to provide emulsification forming the bubbles throughout the adhesive solution.

19. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 9 wherein said coater assembly is a blade coater.

20. A process for making a water resistant air permeable and vapor permeable membrane as claimed in claim 7 wherein said first surfactant is a solvent-free wetting agent to provide emulsification and bubble size ranging from about 4% by weight to about 6% by weight and said second surfactant is a foaming agent ranging from about 1.5% by weight to about 2.0% by weight.