Tire having tread for low temperature performance and wet traction

1. A pneumatic tire having a circumferential rubber tread of a rubber composition comprised of, based on parts by weight per 100 parts by weight elastomer (phr):

(A) 100 parts by weight of a combination of conjugated diene-based elastomers comprised of:

(1) about 10 to about 50 phr of an organic solvent polymerization prepared high Tg styrene/butadiene elastomer having a Tg in a range of from about −40° C. to about −30° C. with a styrene content in a range of from about 30 to about 35 weight percent wherein said high Tg S-SBR is extended with from about 10 to about 38 parts by weight per 100 parts of said high Tg styrene/butadiene elastomer of triglyceride vegetable oil,

(2) about 10 to about 50 phr of aqueous emulsion polymerization prepared styrene/butadiene elastomer having a Tg in a range of from about −65° C. to about −45° C. with a styrene content in a range of from about 15 to about 30 weight percent, and

(3) about 20 to about 60 phr of cis 1,4-polybutadiene rubber having a cis 1,4-isomeric content of at least about 95 percent and having a Tg in a range of from about −100° C. to about −108° C.,

(B) about 50 to about 250 phr of rubber reinforcing filler comprised of a combination of precipitated silica derived from silicon dioxide based inorganic sand or from silicon dioxide containing rice husks and rubber reinforcing carbon black where said reinforcing filler is comprised of from about 2 to about 10 phr of said rubber reinforcing carbon black, wherein said precipitated silica of said reinforcing filler is comprised of at least one of:

(1) pre-hydrophobated precipitated silica comprised of precipitated silica pre-hydrophobated with an alkoxyorganomercaptosilane or bis(3-triethoxysilylpropyl) polysulfide containing an average of from about 2 about 4 connecting sulfur atoms in its polysulfidic bridge to form a composite thereof,

(2) precipitated silica having a nitrogen surface area in a range of from about 140 to about 220 m 2 /g together with a silica coupler having a moiety reactive with hydroxyl groups on said precipitated silica and another different moiety interactive with said diene-based elastomers, and

(3) precipitated silica having a nitrogen surface area in a range of from about 90 to about 130 m 2 /g together with a silica coupler having a moiety reactive with hydroxyl groups on said precipitated silica and another different moiety interactive with said diene-based elastomers,

(C) about 5 to about 45 phr of traction promoting resin comprised of at least one of terpene, coumarone indene and styrene-alphamethylstyrene resins having a softening point within a range of from about 60° C. to about 150° C.

2. The tire of claim 1 wherein said rubber composition contains about 5 to about 50 phr of freely added vegetable triglyceride oil.

3. The tire of claim 2 wherein said freely added triglyceride vegetable oil is comprised of at least one of soybean oil, sunflower oil, rapeseed oil and canola oil.

4. The tire of claim 2 wherein said freely added vegetable triglyceride oil is comprised of soybean oil.

5. The tire of claim 1 wherein said precipitated silica is a pre-hydrophobated precipitated silica comprised of precipitated silica pre-hydrophobated with an alkoxyorganomercaptosilane or bis(3-triethoxysilylpropyl) polysulfide containing an average of from about 2 about 4 connecting sulfur atoms in its polysulfidic bridge to form a composite thereof.

6. The tire of claim 5 wherein said rubber composition contains an additional precipitated silica.

7. The tire of claim 5 wherein said rubber composition contains an additional silica coupling agent comprised of a bis(3-triethoxysilyl propyl) polysulfide having an average of from about 2 to about 4 connecting sulfur atoms in its polysulfide bridge.

8. The tire of claim 1 wherein said precipitated silica is a pre-hydrophobated precipitated silica comprised of precipitated silica pre-hydrophobated with an alkoxyorganomercaptosilane to form a composite thereof.

9. The tire of claim 8 wherein said rubber composition contains an additional precipitated silica.

10. The tire of claim 8 wherein said rubber composition contains an additional precipitated silica together with a silica coupling agent comprised of a bis(3-triethoxysilyl propyl) polysulfide having an average of from about 2 to about 4 connecting sulfur atoms in its polysulfide bridge.

11. The tire of claim 1 wherein said precipitated silica is a precipitated silica having a nitrogen surface area in a range of from about 140 to about 220 m 2 /g together with a silica coupler having a moiety reactive with hydroxyl groups on said precipitated silica and another different moiety interactive with said diene-based elastomers comprised of at least one of alkoxyorganomercaptane and bis (3-triethoxysilylpropyl) containing an average of from about 2 to about 4 connecting sulfur atoms in its polysulfidic bridge.

12. The tire of claim 1 wherein said precipitated silica is a precipitated silica having a nitrogen surface area in a range of from about 90 to about 130 m 2 /g together with a silica coupler having a moiety reactive with hydroxyl groups on said precipitated silica and another different moiety interactive with said diene-based elastomers comprised of at least one of alkoxyorganomercaptane and bis (3-triethoxysilylpropyl) containing an average of from about 2 to about 4 connecting sulfur atoms in its polysulfidic bridge.

13. The tire of claim 1 wherein said triglyceride vegetable oil for said styrene/butadiene elastomer oil extension is comprised of at least one of soybean oil, sunflower oil, rapeseed oil and canola oil.

14. The tire of claim 1 wherein said triglyceride vegetable oil for said styrene/butadiene elastomer oil extension is comprised of soybean oil.

15. The tire of claim 1 wherein said high Tg styrene/butadiene elastomer has an uncured Mooney viscosity (ML1+4), 100° C., in a range of from about 60 to about 120.

16. The tire of claim 1 wherein said high Tg styrene/butadiene elastomer is tin or silicon coupled.

17. The tire of claim 1 wherein said high Tg styrene/butadiene elastomer is a functionalized elastomer containing at least one of amine, siloxy, thiol and carboxyl groups reactive with hydroxyl groups on said precipitated silica.

18. The tire of claim 1 wherein said traction promoting resin is a styrene/alphamethylstyrene resin having a softening point in a range of from about 60° C. to about 125° C.

19. The tire of claim 1 wherein said precipitated silica is derived from silicon dioxide based inorganic sand.

20. The tire of claim 1 wherein said precipitated silica is derived from silicon dioxide containing rice husks.