Pneumatic tire
There is provided a pneumatic tire having improved wet grip performance and fuel efficiency in a good balance. The pneumatic tire is provided with a tread composed of a rubber composition comprising not less than 0.5 part by mass of silica and not less than 5 parts by mass of a resin based on 100 parts by mass of a rubber component comprising 40 to 100% by mass of a styrene-butadiene rubber and 0 to 60% by mass of a butadiene rubber, wherein an adhesive force of the rubber composition measured by the specified adhesion test method is not less than 300 when an adhesive force of a reference rubber composition wherein the whole amount of resin has been replaced by oil is assumed to be 100, and a ratio of a loss tangent tan δ 0° C. at 0° C. of the rubber composition to a loss tangent tan δ 70° C. at 70° C. of the rubber composition (tan δ 0° C. /tan δ 70° C. is from 3.0 to 10.
1. A pneumatic tire with a tread composed of a rubber composition comprising:
not less than 0.5 part by mass of silica and
not less than 5 parts by mass of a resin
based on 100 parts by mass of a rubber component comprising 40 to 100% by mass of a styrene-butadiene rubber and 0 to 60% by mass of a butadiene rubber,
wherein an adhesive force of the rubber composition measured by the following adhesion test method is not less than 300 when an adhesive force of a reference rubber composition wherein the whole amount of resin has been replaced by oil is assumed to be 100,
a loss tangent tan δ 70° C. at 70° C. of the rubber composition is not more than 125 when a loss tangent tan δ 70° C. of the reference rubber composition is assumed to be 100, and
a ratio of a loss tangent tan δ 0° C. at 0° C. of the rubber composition to the loss tangent tan δ 70° C. at 70° C. of the rubber composition (tan δ 0° C. /tan δ 70° C. is from 3.0 to 10,
a softening point of the resin is not lower than 80° C., and
a cis content of the butadiene rubber is not less than 90% by mass,
wherein the adhesion test method comprises:
preparing a test rubber,
conducting a wet friction test and generating an adhesive substance on a surface of the test rubber,
measuring the adhesive substance wherein a volume of the adhesive substance and an adhesive force per unit area of the adhesive substance are measured, and
evaluating an adhesive force of the test rubber based on the volume of the adhesive substance and the adhesive force per unit area of the adhesive substance.
2. The pneumatic tire of claim 1 , wherein a content of the resin is 20 to 50 parts by mass.
3. The pneumatic tire of claim 1 , wherein a content of the butadiene rubber in the rubber component is 15 to 40% by mass.
4. The pneumatic tire of claim 3 , wherein a content of the butadiene rubber in the rubber component is 20 to 40% by mass.