Method for manufacturing sound insulation material, sound insulation material manufactured using the method and carpet for vehicle using the same
Disclosed herein is a method for manufacturing a sound insulation material, a sound insulation material manufactured using this manufacturing method, and a carpet for a vehicle using the sound insulation material, and the sound insulation material is manufactured using a composite resin composition including 30 parts by weight to 70 parts by weight of aluminum oxide, 10 parts by weight to 20 parts by weight of nanoclay, 0.2 parts by weight to 0.8 parts by weight of an antioxidant, and 0.1 parts by weight to 0.5 parts by weight of a lubricant, with respect to 100 parts by weight of a base resin including PE, and the carpet for a vehicle is manufactured by coating the sound insulation material on a carpet fabric material and drying the result.
1. A method for manufacturing a sound insulation material comprising:
preparing a resin composition, which prepares a composite resin composition further including 50 parts by weight of aluminum oxide, 15 parts by weight of nanoclay, 0.2 parts by weight to 0.8 parts by weight of an antioxidant and 30 parts by weight of barium sulfate, with respect to 100 parts by weight of a base resin including PE; and
extrusion molding, which extrusion molds the composite resin composition prepared in the preparing of a resin composition,
wherein the nanoclay is plate-type filler.
2. The method for manufacturing a sound insulation material of claim 1 , wherein 100 parts by weight of the base resin is a mixture of 60 parts by weight to 80 parts by weight of LDPE and 20 parts by weight to 40 parts by weight of rubber.
3. The method for manufacturing a sound insulation material of claim 1 , wherein the preparing of a resin composition further includes 4 parts by weight to 6 parts by weight of a rheology modifier with respect to 100 parts by weight of the base resin including PE to prepare the composite resin composition.
4. The method for manufacturing a sound insulation material of claim 1 , wherein the preparing of a resin composition further includes greater than 0 parts by weight to less than or equal to 40 parts by weight of talc with respect to 100 parts by weight of the base resin including PE to prepare the composite resin composition.
5. The method for manufacturing a sound insulation material of claim 1 , wherein the preparing of a resin composition further includes greater than 0 parts by weight to less than or equal to 25 parts by weight of wollastonite with respect to 100 parts by weight of the base resin including PE to prepare the composite resin composition.
6. The method for manufacturing a sound insulation material of claim 1 , wherein the preparing of a resin composition further includes 1 part by weight to 3 parts by weight of a pigment with respect to 100 parts by weight of the base resin including PE to prepare the composite resin composition.
7. The method for manufacturing a sound insulation material of claim 1 , wherein the preparing of a resin composition includes a first feeding process introducing 0.2 parts by weight to 0.8 parts by weight of an antioxidant and 0.1 parts by weight to 0.5 parts by weight of a lubricant in addition to 100 parts by weight of the base resin, that is, 60 parts by weight to 80 parts by weight of LDPE and 20 parts by weight to 40 parts by weight of rubber, to a first raw material feeding vessel on a fore-end side of a biaxial extruder heated to 150° C. to 240° C.; and a second feeding process introducing 50 parts by weight of aluminum oxide and 15 parts by weight of nanoclay with respect to 100 parts by weight of the base resin to a second raw material feeding vessel located at the middle of the biaxial extruder after the first feeding process.
8. The method for manufacturing a sound insulation material of claim 7 , wherein, in the first feeding process, at least any one of 4 parts by weight to 6 parts by weight of a rheology modifier and 1 part by weight to 3 parts by weight of a pigment with respect to 100 parts by weight of the base resin is further included and introduced to the first raw material feeding vessel.
9. The method for manufacturing a sound insulation material of claim 8 , wherein, in the second feeding process, at least any one of 30 parts by weight of barium sulfate, greater than 0 parts by weight and less than or equal to 40 parts by weight of talc, greater than 0 parts by weight and less than or equal to 25 parts by weight of ferrite, and greater than 0 parts by weight and less than or equal to 25 parts by weight of wollastonite, with respect to 100 parts by weight of the base resin may be further included and introduced to the second raw material feeding vessel.