Power storage device
A power storage device with reduced initial irreversible capacity is provided. The power storage device includes a positive electrode including a positive electrode current collector and a positive electrode active material layer, a negative electrode including a negative electrode current collector and a negative electrode active material layer, and an electrolyte solution. In the negative electrode active material layer, the content percentage of a carbon material with an R value of 1.1 or more is less than 2 wt %. The R value refers to a ratio of a peak intensity I 1360 to a peak intensity I 1580 (I 1360 /I 1580 ). The peak intensity I 1360 and the peak intensity I 1580 are observed by Raman spectrometry at a Raman shift of 1360 cm −1 and a Raman shift of 1580 cm −1 , respectively. The electrolyte solution contains a lithium ion and an ionic liquid composed of an organic cation and an anion.
1. A method for manufacturing a power storage device comprising the steps of:
mixing a carbon material and binder with a solvent to form a paste;
applying the paste on a current collector;
drying the paste on the current collector to form a negative electrode; and
impregnating a positive electrode, the negative electrode, and a separator with an electrolyte solution containing a lithium ion and an ionic liquid composed of an organic cation and an anion,
wherein a melting point of the ionic liquid is −10° C. or lower,
wherein a content percentage of the carbon material with the R value of 1.1 or more is less than 2 wt % in the negative electrode,
wherein the R value is a ratio of a peak intensity I 1360 to a peak intensity I 1580 (I 1360 /I 1580 ), the peak intensity I 1360 and the peak intensity I 1580 are observed by Raman spectrometry at a Raman shift of 1360 cm −1 and a Raman shift of 1580 cm −1 , respectively.
2. The method for manufacturing a power storage device according to claim 1 ,
wherein the organic cation is a quaternary ammonium cation, a tertiary sulfonium cation, a quaternary phosphonium cation, an imidazolium cation, or a pyridinium cation.
3. The method for manufacturing a power storage device according to claim 1 ,
wherein the ionic liquid is represented by a General Formula (G1),
wherein R 1 to R 6 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
4. The method for manufacturing a power storage device according to claim 1 ,
wherein the ionic liquid is represented by a General Formula (G2),
wherein R 7 to R 13 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
5. The method for manufacturing a power storage device according to claim 1 ,
wherein the ionic liquid includes two aliphatic rings and is represented by a General Formula (G3),
wherein n and m are greater than or equal to 1 and less than or equal to 3,
wherein α is greater than or equal to 0 and less than or equal to 4 when n is 1, α is greater than or equal to 0 and less than or equal to 5 when n is 2, and α is greater than or equal to 0 and less than or equal to 6 when n is 3,
wherein β is greater than or equal to 0 and less than or equal to 4 when m is 1, β is greater than or equal to 0 and less than or equal to 5 when m is 2, and β is greater than or equal to 0 and less than or equal to 6 when m is 3,
wherein “α or β is 0” means that at least one of the two aliphatic rings is unsubstituted, and a case where both α and β are 0 is excluded,
wherein X or Y is a substituent which is a straight chain or lateral chain alkyl group having 1 to 4 carbon atoms, a straight chain or lateral chain alkoxy group having 1 to 4 carbon atoms, or a straight chain or lateral chain alkoxyalkyl group having 1 to 4 carbon atoms, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
6. A method for manufacturing a power storage device comprising the steps of:
mixing a carbon material comprising graphite and binder with a solvent to form a paste;
applying the paste on a current collector;
drying the paste on the current collector to form a negative electrode; and
impregnating a positive electrode, the negative electrode, and a separator with an electrolyte solution containing a lithium ion and an ionic liquid composed of an organic cation and an anion,
wherein a content percentage of the carbon material with the R value of 1.1 or more is less than 2 wt % in the negative electrode,
wherein the R value is a ratio of a peak intensity I 1360 to a peak intensity I1580 (I 1360 /I 1580 ), the peak intensity I 1360 and the peak intensity I 1580 are observed by Raman spectrometry at a Raman shift of 1360 cm −1 and a Raman shift of 1580 cm −1 , respectively.
7. The method for manufacturing a power storage device according to claim 6 ,
wherein the organic cation is a quaternary ammonium cation, a tertiary sulfonium cation, a quaternary phosphonium cation, an imidazolium cation, or a pyridinium cation.
8. The method for manufacturing a power storage device according to claim 6 ,
wherein the ionic liquid is represented by a General Formula (G1),
wherein R 1 to R 6 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
9. The method for manufacturing a power storage device according to claim 6 ,
wherein the ionic liquid is represented by a General Formula (G2),
wherein R 7 to R 13 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
10. The method for manufacturing a power storage device according to claim 6 ,
wherein the ionic liquid includes two aliphatic rings and is represented by a General Formula (G3),
wherein n and m are greater than or equal to 1 and less than or equal to 3,
wherein α is greater than or equal to 0 and less than or equal to 4 when n is 1, α is greater than or equal to 0 and less than or equal to 5 when n is 2, and α is greater than or equal to 0 and less than or equal to 6 when n is 3,
wherein β is greater than or equal to 0 and less than or equal to 4 when m is 1, β is greater than or equal to 0 and less than or equal to 5 when m is 2, and β is greater than or equal to 0 and less than or equal to 6 when m is 3,
wherein “α or β is 0” means that at least one of the two aliphatic rings is unsubstituted, and a case where both α and β are 0 is excluded,
wherein X or Y is a substituent which is a straight chain or lateral chain alkyl group having 1 to 4 carbon atoms, a straight chain or lateral chain alkoxy group having 1 to 4 carbon atoms, or a straight chain or lateral chain alkoxyalkyl group having 1 to 4 carbon atoms, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
11. A method for manufacturing a power storage device comprising the steps of:
mixing a carbon material comprising graphene and binder with a solvent to form a paste;
applying the paste on a current collector;
drying the paste on the current collector to form a negative electrode; and
impregnating a positive electrode, the negative electrode, and a separator with an electrolyte solution containing a lithium ion and an ionic liquid composed of an organic cation and an anion,
wherein a content percentage of the carbon material with the R value of 1.1 or more is less than 2 wt % in the negative electrode,
wherein the R value is a ratio of a peak intensity I 1360 to a peak intensity I 1580 (I 1360 /I 1580 ), the peak intensity I 1360 and the peak intensity I 1580 are observed by Raman spectrometry at a Raman shift of 1360 cm −1 and a Raman shift of 1580 cm −1 , respectively.
12. The method for manufacturing a power storage device according to claim 11 ,
wherein the organic cation is a quaternary ammonium cation, a tertiary sulfonium cation, a quaternary phosphonium cation, an imidazolium cation, or a pyridinium cation.
13. The method for manufacturing a power storage device according to claim 11 ,
wherein the ionic liquid is represented by a General Formula (G1),
wherein R 1 to R 6 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
14. The method for manufacturing a power storage device according to claim 11 ,
wherein the ionic liquid is represented by a General Formula (G2),
wherein R 7 to R 13 separately represent an alkyl group having 1 to 20 carbon atoms, a methoxy group, a methoxymethyl group, a methoxyethyl group, or a hydrogen atom, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.
15. The method for manufacturing a power storage device according to claim 11 ,
wherein the ionic liquid includes two aliphatic rings and is represented by a General Formula (G3),
wherein n and m are greater than or equal to 1 and less than or equal to 3,
wherein α is greater than or equal to 0 and less than or equal to 4 when n is 1, α is greater than or equal to 0 and less than or equal to 5 when n is 2, and α is greater than or equal to 0 and less than or equal to 6 when n is 3,
wherein β is greater than or equal to 0 and less than or equal to 4 when m is 1, β is greater than or equal to 0 and less than or equal to 5 when m is 2, and β is greater than or equal to 0 and less than or equal to 6 when m is 3,
wherein “α or β is 0” means that at least one of the two aliphatic rings is unsubstituted, and a case where both α and β are 0 is excluded,
wherein X or Y is a substituent which is a straight chain or lateral chain alkyl group having 1 to 4 carbon atoms, a straight chain or lateral chain alkoxy group having 1 to 4 carbon atoms, or a straight chain or lateral chain alkoxyalkyl group having 1 to 4 carbon atoms, and
wherein A − represents a monovalent amide anion, a monovalent methide anion, a perfluoroalkylsulfonate anion, tetrafluoroborate, perfluoroalkylborate, hexafluorophosphate, or perfluoroalkylphosphate.