Disclosed is a method for readily and inexpensively producing zeolite without using an organic structure-directing agent (organic SDA). Specifically disclosed is a method whereby a gel containing a silica source, an alumina source, an alkaline source and water is reacted with zeolite seed crystals, to produce a zeolite with the same kind of skeletal structure as the zeolite. The gel used is a gel of a composition whereby, when a zeolite is synthesized from this gel only, the synthesized zeolite comprises at least one of the kinds of composite building units of the target zeolite.
1. A method of producing a zeolite comprising:
reacting a gel and zeolite seed crystals to produce a zeolite having the same kind of skeletal structure as the zeolite seed crystals;
wherein:
the gel comprises a silica source, an alumina source, an alkali source and water;
the gel is capable of synthesizing a zeolite without the use of the zeolite seed crystals, wherein the zeolite synthesized without the use of the zeolite seed crystals comprises one or more building units of zeolite;
the zeolite seed crystals comprise one or more composite building units of zeolite;
the zeolite seed crystals and the zeolite synthesized without the use of zeolite seed crystals comprise at least one equivalent composite building unit of zeolite;
wherein the reacting step occurs without the use of an organic structure-directing agent;
wherein the zeolite produced is beta zeolite;
wherein the gel has a composition of:
SiO 2 /Al 2 O 3 =12 to 20,
Na 2 O/SiO 2 =0.1 to 0.25,
H 2 O/SiO 2 =10 to 25,
and wherein an amount of the zeolite seed crystals is 1 weight % to 20 weight % with respect to the silica component included in the gel.
2. The method of producing a zeolite according to claim 1 ,
wherein the zeolite synthesized without the use of zeolite seed crystals has a different kind of skeletal structure as the zeolite seed crystals.
3. The method of producing a zeolite according to claim 1 ,
wherein, as a post treatment, dealumination of the zeolite is carried out by mixing the zeolite and an aqueous solution of citric acid or a salt thereof, and heating a mixed aqueous solution under an autogenous pressure.