Exhaust gas purifying catalyst
To reduce an OSC material, while maintaining necessary OSC capacity; and to improve heat resistance and reactivity of a precious metal. Proposed is an exhaust gas purifying catalyst which comprises a first catalyst layer that is formed on the surface of a substrate that is formed of a ceramic or a metal, and a second catalyst layer that is formed on the upper side of the first catalyst layer. The first catalyst layer comprises a precious metal, an OSC material and an alumina, and the OSC material and the alumina are comprised at a mass ratio of OSC material:alumina=1:7 to 1:3. The second catalyst layer comprises a precious metal, an OSC material and an alumina, and the OSC material and the alumina are comprised at a mass ratio of OSC material:alumina=1:1 to 10:0.
1. An exhaust gas purifying catalyst having a first catalyst layer which is formed on a surface of a substrate comprising a ceramic or a metal and a second catalyst layer which is formed on the upper side of the first catalyst layer,
wherein the first catalyst layer comprises a precious metal, an OSC material and an alumina, and the OSC material and the alumina are comprised at a mass ratio of OSC material:alumina=1:7 to 1:3, and
the second catalyst layer comprises a precious metal, an OSC material and an alumina, and the OSC material and the alumina are comprised at a mass ratio of OSC material:alumina=2.2:1 to 10:1.
2. The exhaust gas purifying catalyst according to claim 1 , wherein an average particle size (D50) of the alumina in the first catalyst layer is 10 to 16 μm, and an average particle size (D50) of the OSC material in the first catalyst layer is 3 to 12 μm.
3. The exhaust gas purifying catalyst according to claim 2 , wherein a mass ratio of the OSC material and the alumina in the first catalyst layer is OSC material:alumina=1:5 to 1:3.
4. The exhaust gas purifying catalyst according to claim 2 , wherein a material of the substrate is stainless steel (SUS).
5. The exhaust gas purifying catalyst according to claim 2 , having a first peak within a range of a void volume diameter of 15 to 35 nm and a second peak within a range of a void volume diameter of 50 to 200 nm, in a range of void volume diameter of 5 to 200 nm in a logarithmic differentiation void volume distribution measured by a mercury intrusion porosimeter.
6. The exhaust gas purifying catalyst according to claim 2 , wherein a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm.
7. The exhaust gas purifying catalyst according to claim 2 , wherein a pore diameter of the OSC material in the second catalyst layer is 50 to 90 nm.
8. The exhaust gas purifying catalyst according to claim 1 , wherein a mass ratio of the OSC material and the alumina in the first catalyst layer is OSC material:alumina=1:5 to 1:3.
9. The exhaust gas purifying catalyst according to claim 8 , wherein a material of the substrate is stainless steel (SUS).
10. The exhaust gas purifying catalyst according to claim 8 , having a first peak within a range of a void volume diameter of 15 to 35 nm and a second peak within a range of a void volume diameter of 50 to 200 nm, in a range of void volume diameter of 5 to 200 nm in a logarithmic differentiation void volume distribution measured by a mercury intrusion porosimeter.
11. The exhaust gas purifying catalyst according to claim 8 , wherein a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm.
12. The exhaust gas purifying catalyst according to claim 1 , wherein a material of the substrate is stainless steel (SUS).
13. The exhaust gas purifying catalyst according to claim 12 , having a first peak within a range of a void volume diameter of 15 to 35 nm and a second peak within a range of a void volume diameter of 50 to 200 nm, in a range of void volume diameter of 5 to 200 nm in a logarithmic differentiation void volume distribution measured by a mercury intrusion porosimeter.
14. The exhaust gas purifying catalyst according to claim 12 , wherein a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm.
15. The exhaust gas purifying catalyst according to claim 1 , having a first peak within a range of a void volume diameter of 15 to 35 nm and a second peak within a range of a void volume diameter of 50 to 200 nm, in a range of void volume diameter of 5 to 200 nm in a logarithmic differentiation void volume distribution measured by a mercury intrusion porosimeter.
16. The exhaust gas purifying catalyst according to claim 15 , wherein a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm.
17. The exhaust gas purifying catalyst according to claim 1 , wherein a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm.
18. The exhaust gas purifying catalyst according to claim 1 , wherein a pore diameter of the OSC material in the second catalyst layer is 50 to 90 nm.
19. The exhaust gas purifying catalyst according to claim 1 , wherein an average particle size (D50) of the alumina in the first catalyst layer is 13 to 16 μm, and an average particle size (D50) of the OSC material in the first catalyst layer is 3 to 12 μm.
20. The exhaust gas purifying catalyst according to claim 1 , wherein
a pore diameter of the alumina in the first catalyst layer is 15 to 35 nm,
a pore diameter of the OSC material in the second catalyst layer is 50 to 90 nm,
a content of the alumina is larger than a content of the OSC material in the first catalyst layer, and
a content of the OSC material is larger than a content of the alumina in the second catalyst layer.