Method of annealing aluminium alloy sheet material
A method for continuously annealing aluminum alloy sheet at final thickness by continuously moving heat-treatable AlMgSi aluminum alloy sheet through a continuous annealing furnace arranged to heat the moving aluminum sheet to a set soaking temperature (T SET ) in the temperature range of 500° C. to 590° C., the continuous annealing furnace has an entry section and an exit section, the moving aluminum sheet moves substantially horizontally through the continuous annealing furnace, wherein the moving aluminum sheet is rapidly cooled on leaving the exit section, wherein before or near the entry section of the continuous annealing furnace the moving aluminum sheet is pre-heated to a temperature of 5° C. to 100° C. below the T SET using an average heat-up rate as function of sheet thickness of at least Y=−31·ln(X)+50, wherein Y is the heat-up rate in ° C./sec and X is the sheet thickness in mm.
1. A method for continuously annealing aluminium alloy sheet at final thickness, comprising:
continuously moving uncoiled heat-treatable AlMgSi aluminum alloy sheet, having a sheet thickness, in the direction of its length through a continuous annealing furnace arranged to heat the moving aluminium sheet to a set soaking temperature (TSET) in a temperature range of 500° C. to 590° C., the continuous annealing furnace has an entry section and an exit section, wherein the moving aluminium sheet moves substantially horizontally through the continuous annealing furnace,
wherein the continuous annealing furnace is heated by convective heating, and
wherein the moving aluminium sheet is rapidly cooled from TSET to below about 100° C. on leaving the exit section, and
wherein before or near the entry section of the continuous annealing furnace the moving aluminium sheet is pre-heated to a temperature of 5° C. to 100° C. below the TSET using an average heat-up rate as function of the sheet thickness of at least Y=−31·ln(X)+50, wherein “Y” is the heat-up rate in ° C./sec and “X” is the sheet thickness in mm.
2. The method according to claim 1 , wherein before or at the entry section of the continuous annealing furnace the moving aluminium sheet is pre-heated to a temperature of 5° C. to 100° C. below the TSET using an average heat-up rate as function of the sheet thickness of at least Y=−50·ln(X)+80, and more preferably of at least Y=−62·ln(X)+100, wherein Y is the heat-up rate in ° C./sec and X is the sheet thickness in mm.
3. The method according to claim 1 , wherein the pre-heating is per-formed inductively by induction heating.
4. The method according to claim 1 , wherein the pre-heating is done inductively by a transverse flux induction heating device.
5. The method according to claim 1 , wherein the aluminium alloy sheet at final gauge has a thickness in a range of 0.3 to 4.5 mm.
6. The method according to claim 1 , wherein the moving aluminium sheet moves substantially horizontally through the continuous annealing furnace over a length of at least 20 meters.
7. The method according to claim 1 , wherein a soaking time of the moving aluminium sheet at TSET is at least 1 seconds.
8. The method according to claim 1 , wherein the moving aluminium sheet is pre-heated to a temperature of 5° C. to 75° C. below the TSET.
9. The method according to claim 1 , wherein the moving aluminium sheet is pre-heated to a temperature of 10° C. to 100° C. below the TSET.
10. The method according to claim 1 , wherein the continuous annealing furnace is arranged to heat the moving aluminium sheet to a set soaking temperature (TSET) in a temperature range of 520° C. to 580° C.
11. The method according to claim 1 , wherein the moving aluminium sheet is rapidly cooled or quenched after leaving the exit section and is stretched up to 2%, by tension levelling.
12. The method according to claim 11 , wherein the stretched and moving aluminium sheet is subsequently cleaned and provided with a passivation coating.
13. The method according to claim 12 , wherein the stretched aluminium sheet having a passivation coating is heated-treated in a pre-bake heat treatment.
14. The method according to claim 1 , wherein convective heating of the continuous annealing furnace is gas fired.
15. The method according claim 1 , wherein the aluminium alloy sheet at final gauge has a thickness in the range of 0.7 to 4.5 mm.
16. The method according claim 1 , wherein the moving aluminium sheet moves substantially horizontally through the continuous annealing furnace over a length of at least 40 meters.
17. The method according to claim 1 , wherein a soaking time of the moving aluminium sheet at TSET is at least 5 seconds.
18. The method according to claim 1 , wherein a soaking time of the moving aluminium sheet at TSET is at least 20 seconds.
19. The method according to claim 1 , wherein the moving aluminium sheet is pre-heated to a temperature of 5° C. to 60° C. below the TSET.
20. The method according to claim 1 , wherein the moving aluminium sheet is pre-heated to a temperature of 10° C. to 75° C. below the TSET.
21. The method according to claim 1 , wherein the moving aluminium sheet is pre-heated to a temperature of 10° C. to 60° C. below the TSET.
22. The method according to claim 1 , wherein the moving aluminium sheet is rapidly cooled or quenched after leaving the exit section and is stretched in a range of 0.1% to 0.3%, by tension levelling.