Surface structure forming method for zirconia-based ceramics, and zirconia-based ceramics
Provided herein is a method for forming a periodic microstructure on a surface of zirconia-based ceramics, which are not easily mechanically workable, without causing thermal adverse effects. A zirconia-based ceramic having a surface periodic microstructure is also provided. A linearly or circularly polarized laser beam is irradiated to a zirconia-based ceramic surface, and periodic irregularities are formed in a spot of the laser beam. Stripe-pattern irregularities parallel to the direction of polarization can be formed in a spot of a laser beam by irradiating a linearly polarized ultrashort pulsed-laser beam to a zirconia-based ceramic surface. A mesh-like raised region and a dot-like recessed region can be periodically formed by irradiating a circularly polarized ultrashort pulsed-laser beam to a ceramic surface.
1. A surface structure forming method for zirconia-based ceramics,
the method comprising irradiating a laser beam to a zirconia-based ceramic surface with a predetermined shot number in one location to form periodic irregularities in a spot of the laser beam irradiation,
wherein the irradiation of the laser beam with the predetermined shot number in one location forms a periodic structure region with the periodic irregularities and an ablated region where ablation mark is present with no periodic structure, surrounding the periodic structure region in the spot of the laser beam irradiation.
2. The method according to claim 1 , wherein the laser beam is condensed to a space restricting mask of a shape that enables irradiating only a beam region that forms the periodic structure, and an image conforming to the shape is transferred to an optical system, and applied to the zirconia-based ceramic surface to lay down a plurality of periodic structure forming regions of said shape.
3. The method according to claim 1 ,
wherein the method further comprising repeating the irradiation of the laser beam with the predetermined shot number in one location to form the periodic irregularities in the spot of the laser beam irradiation by moving the laser beam to change the location such that regions of the spots of the laser beam irradiations partially overlap one another, are positioned adjacent to one another, or are positioned away from one another to increase an area of the periodic irregularities.
4. The method according to claim 3 ,
wherein the method further comprising restricting a shape of the laser beam with the space restricting mask, and irradiating to a three-dimensional surface, to form a periodic structure over a wide area without a gap of a zirconia base material surface.
5. The method according to claim 4 ,
wherein the shape of the laser beam is triangular, pentagonal, hexagonal, or other polygonal spatial shapes.
6. The method according to claim 1 , wherein a period of the periodic irregularities is not dependent on an incident angle of the laser beam when an s-polarized laser beam is used and the period of the periodic irregularities increases with increase of the incident angle of the laser beam when a p-polarized laser beam is used.
7. The method according to claim 1 , wherein the irradiation is operated with a value of an etch rate/a wavelength of the pulsed-laser beam set to be 0.16 to 0.34.
8. A surface structure forming method for a zirconia-based ceramic surface,
the method comprising irradiating a linearly polarized ultrashort pulsed-laser beam to the ceramic surface with a predetermined shot number in one location to form periodic irregularities having a stripe-pattern extending parallel to a direction of polarization of the linearly polarized light in a spot of the laser beam,
wherein the irradiation of the laser beam with the predetermined shot number in one location forms a periodic structure region with the periodic irregularities and an ablated region where ablation mark is present with no periodic structure, surrounding the periodic structure region in the spot of the laser beam irradiation.
9. The method according to claim 8 , wherein the laser beam is condensed to a space restricting mask of a shape that enables irradiating only a beam region that forms the periodic structure, and an image conforming to the shape is transferred to an optical system, and applied to the zirconia-based ceramic surface to lay down a plurality of periodic structure forming regions of said shape.
10. The method according to claim 8 ,
wherein the method further comprising repeating the irradiation of the laser beam with the predetermined shot number in one location to form the periodic irregularities in the spot of the laser beam irradiation by moving the laser beam to change the location such that regions of the spots of the laser beam irradiations partially overlap one another, are positioned adjacent to one another, or are positioned away from one another to increase an area of the periodic irregularities.
11. The method according to claim 10 ,
wherein the method further comprising restricting a shape of the laser beam with the space restricting mask, and irradiating to a three-dimensional surface, to form a periodic structure over a wide area without a gap of a zirconia base material surface.
12. The method according to claim 11 ,
wherein the shape of the laser beam is triangular, pentagonal, hexagonal, or other polygonal spatial shapes.
13. The method according to claim 8 , wherein a period of the periodic irregularities is not dependent on an incident angle of the laser beam when an s-polarized laser beam is used and the period of the periodic irregularities increases with increase of the incident angle of the laser beam when a p-polarized laser beam is used.
14. The method according to claim 8 , wherein the irradiation is operated with a value of an etch rate/a wavelength of the pulsed-laser beam set to be 0.16 to 0.34.
15. A surface structure forming method for a zirconia-based ceramic surface,
the method comprising irradiating a circularly polarized ultrashort pulsed-laser beam to the ceramic surface with a predetermined shot number in one location to form a mesh pattern having periodic raised regions with dot-shaped recessed regions in a spot of the laser beam
wherein the irradiation of the laser beam with the predetermined shot number in one location forms a periodic structure region with the mesh pattern and an ablated region where ablation mark is present with no periodic structure, surrounding the periodic structure region in the spot of the laser beam irradiation.
16. The method according to claim 15 , wherein the laser beam is condensed to a space restricting mask of a shape that enables irradiating only a beam region that forms the periodic structure, and an image conforming to the shape is transferred to an optical system, and applied to the zirconia-based ceramic surface to lay down a plurality of periodic structure forming regions of said shape.
17. The method according to claim 15 ,
wherein the method further comprising repeating the irradiation of the laser beam with the predetermined shot number in one location to form the mesh pattern in the spot of the laser beam irradiation by moving the laser beam to change the location such that regions of the spots of the laser beam irradiations partially overlap one another, are positioned adjacent to one another, or are positioned away from one another to increase an area of the periodic irregularities.
18. The method according to claim 17 ,
wherein the method comprising restricting a shape of the laser beam with the space restricting mask, and irradiating to a three-dimensional surface, to form a periodic structure over a wide area without a gap of a zirconia base material surface.
19. The method according to claim 18 ,
wherein the shape of the laser beam is triangular, pentagonal, hexagonal, or other polygonal spatial shapes.
20. The method according to claim 15 , wherein the irradiation is operated with a value of an etch rate/a wavelength of the pulsed-laser beam set to be 0.16 to 0.34.