Snap Ability Modifier For Biogradable Polyesters
The invention relates to an article comprising a monolayer or multilayer thermoplastic material, said material comprises (i) 38.00 to 99.95%, preferably 67.00 to 99.9%, more preferably 57.00 to 99.85%, by weight of polylactic acid, (ii) 0.05 to 4.90%, preferably 0.10 to 2.90%, more preferably 0.15 to 2.00%, even more preferably 0.2 to 1.00%, most preferably 0.25 to 0.75%, by weight of an epoxidized vegetable oil; (iii) 0 to 60.00%, preferably 0 to 40.00%, more preferably 0 to 30.00%, by weight of further additives selected from the group consisting of impact modifiers, plasticisers, crosslinking agents, foaming agents, fillers, colorants, stabilizers, lubricants, and mixtures thereof, the weight percentages being relative to total weight of the monolayer or multilayer thermoplastic material and adding up to 100%.
1 . An article comprising a monolayer or multilayer thermoplastic material, wherein the material comprises
(i) 38.00 to 99.95% by weight of polylactic acid,
(ii) 0.05 to 4.90% by weight of an epoxidized vegetable oil;
(iii) 0 to 60.00% by weight of further additives selected from the group consisting of impact modifiers, plasticisers, crosslinking agents, foaming agents, fillers, colorants, stabilizers, lubricants, and mixtures thereof,
the weight percentages being relative to total weight of the monolayer or multilayer thermoplastic material and adding up to 100%.
2 . An article as claimed in claim 1 , wherein the material comprises:
(i) 88.00 to 99.85% by weight of the polylactic acid,
(ii) 0.15 to 2.00% by weight of the epoxidized vegetable oil;
(iii) 0 to 10.00% by weight of the further additives selected from the group consisting of impact modifiers, plasticisers, crosslinking agents, foaming agents, fillers, colorants, stabilizers, lubricants, and mixtures thereof,
the weight percentages being relative to total weight of the monolayer or multilayer thermoplastic material and adding up to 100%.
3 . The article as claimed in claim 1 , wherein the vegetable oil is a triglyceride of saturated or unsaturated fatty acid esters with a chain length from C 6 to C 22 .
4 . The article as claimed in claim 1 , wherein the epoxidized vegetable oil is epoxidized soybean oil, epoxidized methyl soyate, epoxidized linseed oil, epoxidized tall oil, epoxidized peanut oil, epoxidized castor oil, epoxidized coconut oil, epoxidized palm oil, epoxidized corn oil, epoxidized safflower oil, or a mixture thereof.
5 . The article as claimed in claim 1 , wherein the article is a multilayer article comprising (A) at least one layer A of non-foamed polylactic acid and (B) at least one layer B of foamed polylactic acid, wherein either (A), or (B), or (A) and (B) contain the epoxidized vegetable oil.
6 . The article as claimed in claim 1 , wherein the article is a plastic sheet.
7 . The article as claimed in any of claim 1 wherein the article comprises a thermoformed part.
8 . The article as claimed in claim 7 , wherein the article is a container.
9 . The article as claimed in claim 8 , being a container ( 1 ) having a hollow body ( 2 ) and optionally at least one flange ( 10 ), the hollow body defining said the thermoformed part, the hollow body having an opening ( 8 ).
10 . The article as claimed in claim 9 , wherein the hollow body ( 2 ) is at least partially covered by a banderole.
11 . The article as claimed in claim 8 , wherein the container is a cup, in a multipack form or in an individual cup form.
12 . An article as claimed in claim 1 , wherein the material consists of:
(i) 38.00 to 99.95% by weight of the polylactic acid,
(ii) 0.05 to 4.90% by weight of an the epoxidized vegetable oil;
(iii) 0 to 60.00% by weight of further additives selected from the group consisting of impact modifiers, plasticisers, crosslinking agents, foaming agents, fillers, colorants, stabilizers, lubricants, and mixtures thereof,
the weight percentages being relative to total weight of the monolayer or multilayer thermoplastic material and adding up to 100%.
13 . A process for manufacturing an article as claimed in claim 1 , comprising the steps of mixing polylactic acid, epoxidized vegetable oil and optionally the further additives in an extruder under heating to a temperature of 150 to 250° C. to form a mixture and extruding or co-extruding the mixture.
14 . A process according to claim 13 , further comprising a step of thermoforming.
15 . The process as claimed in claim 13 , wherein the epoxidized vegetable oil is added in form of a masterbatch.
16 . A snap ability modifier in optionally thermoformed polylactic acid sheets comprising an epoxidized vegetable oil.
17 . The article as claimed in claim 6 , wherein the thermoformed part has a total stretch ratio of at least 2.5.