METHOD FOR PREPARING POLYETHYLENE TEREPHTHALATE POLYMER, POLYETHYLENE TEREPHTHALATE POLYMER YARN AND CAR MAT COMPRISING THE SAME
The present invention relates to a method for producing a polyethylene terephthalate polymer having improved abrasion resistance by introducing an inorganic particle (metal) in addition to ethylene glycol (EG, Ethyleneglycol) and terephthalic acid (TPA, terephthalic acid) forming a conventional polyethylene terephthalate bond, and a yarn and a car mat produced by using the polyethylene terephthalate polymer produced by the above-mentioned production method. When the yarn and the car mat are produced by using the above-mentioned polyethylene terephthalate polymer, the density of the yarn is improved and the abrasion resistance of the car mat can be improved.
1 . A method for preparing a polyethylene terephthalate polymer, characterized by comprising the steps of:
preparing a slurry by mixing ethylene glycol (EG, Ethyleneglycol) and terephthalic acid (TPA, Terephthalic acid);
esterifying the slurry; and
polycondensating the slurry,
wherein after or before the esterifying or before the polycondensating, a master batch including inorganic particles or an inorganic particle is inserted.
2 . The method for preparing the polyethylene terephthalate polymer according to claim 1 ,
wherein the inorganic particles are at least one selected from the group comprising barium sulfate, silica, kaolin, aluminum oxide (Al2O3), TiO2, calcium carbonate (CaCO3), mica, zeolite, talc, glass beads powder and calcium phosphate.
3 . The method for preparing the polyethylene terephthalate polymer according to claim 1 ,
wherein the inorganic particles are added in an amount of 0.01 to 5 weight %.
4 . The method for preparing the polyethylene terephthalate polymer according to claim 1 ,
wherein the inorganic particle has an average particle diameter of 0.1 to 10 μm.
5 . The method for preparing the polyethylene terephthalate polymer according to claim 1 ,
wherein the polyethylene terephthalate polymer has intrinsic viscosity (IV) of 0.8 or more.
6 . A polyethylene terephthalate polymer produced by the method according to claim 1 .
7 . A polyethylene terephthalate yarn produced by the polyethylene terephthalate polymer according to claim 6 ,
wherein the denier of the yarn is 800 to 1,500 denier.
8 . A car mat comprising the polyethylene terephthalate yarn according to claim 7 .