Welding of steel blanks

1. A method for joining a first steel blank and a second steel blank, at least one of the first or second steel blanks comprising a layer of aluminum or of an aluminum alloy, the method comprising:

providing a first support for the first steel blank and a second support for the second steel blank, the first and second supports being made of a magnetic material and being arranged distanced apart by a central space provided between them,

providing a first coil winding around the first support,

arranging the first blank on the first support and the second blank on the second support, such that a butt end of the first blank that is facing the second blank is brought into contact with a butt end of the second blank that is facing the first blank defining a contacting area that closes a path for magnetic flux between the first and second supports and through the first and second blanks when in use,

providing a laser system, wherein the laser system comprises one or more optical elements and a laser source for generating a laser beam;

applying the laser beam onto the contacting area using the laser system, while simultaneously

applying an alternating current to the first coil winding such that an alternating magnetic field is created across the contacting area in a direction from the first blank to the second blank,

thereby allowing non-magnetic aluminum particles to fall from a weld zone formed between the first blank and the second blank.

2. The method of claim 1 , wherein the first steel blank and/or the second steel blank is made from a boron alloyed steel coated with aluminum silicon.

3. The method of claim 1 , further comprising providing a second coil winding around the second support and applying an alternating current to the second coil winding such that an alternating magnetic field is created and the generated alternating magnetic fields by the first and second coils are inverted.

4. The method of claim 1 , wherein a lower base made of a magnetic or magnetisable material is provided in contact with a lower side of the first and second supports, the lower side of each of the first and second supports being opposite to a side of the first and second supports on which the first and second blanks are to be placed.

5. The method of claim 1 , wherein a collector plate is provided in a central space underneath the contacting area of the first and second blanks for collecting aluminum particles.

6. The method of claim 1 , wherein a frequency of the alternating current is 50 or 60 Hz.

7. The method of claim 1 , wherein the laser system is arranged such that the laser beam impacts perpendicular to the blanks.

8. The method of claim 1 , wherein the laser system comprises a laser with a power of between 3 kW and 16 kW.

9. The method of claim 8 , wherein the laser system comprises an Nd-YAG laser.

10. A method for forming a product comprising:

forming a blank including a method of joining a first and a second steel blanks according to the method of claim 1 ,

heating the blank, and

hot deforming and subsequent quenching of the heated blank.

11. The method of claim 1 , wherein the laser system comprises a laser with a power of between 4 kW and 8 kW.