Composition for polymeric chain extension
The present invention relates to a composition comprising at least one compound of the formula (1) wherein R 1 , R 2 and R 3 are the same or different and denote a C 1 -C 10 -alkyl, and at least one carrier resin.
1. A composition comprising at least one compound of the formula (1)
wherein R 1 , R 2 and R 3 are the same or different and are a C 1 -C 10 -alkyl, and
at least one carrier resin which is selected from the group consisting of polyethylene, polyethylene-norbornene copolymers, polypropylene, polybutylene, polymethyl pentene, polyethylene-vinyl acetate copolymers, polycarbonate, polystyrene, polystyrene block copolymers, polybutadiene, polyisoprene, polyethylene-butylene, polyacrylates, polyvinyl chloride, chlorinated polyethylene, polyvinylidene chloride, polyethylene-acrylate copolymers, acrylonitrile-butadiene-styrene copolymers, and mixtures thereof,
wherein the compound of formula (1) is present in an amount of between 1.0 and 99.9 wt.-% relative to the total weight of the composition.
2. The composition as claimed in claim 1 , wherein R 1 , R 2 and R 3 are the same or different and are a C 1 -C 2 -alkyl.
3. The composition as claimed in claim 1 , wherein R 1 , R 2 and R 3 are methyl.
4. The composition as claimed in claim 1 , wherein the carrier resin is a polycarbonate or polypropylene.
5. The composition as claimed in claim 1 , wherein the compound of formula (1) is present in an amount of between 5.0 to 50.0 wt.-%, relative to the total weight of the composition.
6. The composition as claimed in claim 1 , wherein the compound of formula (1) is present in an amount of between 5.0 and 25.0 wt.-%, relative to the total weight of the concentrate composition.
7. A method for imparting chain extension properties to a let down polymer having at least one carboxyl reactive group, the method comprising melt compounding with the let down polymer a composition comprising at least one chain extender and at least one carrier resin as claimed in claim 1 in a thermoplastic forming apparatus at a temperature sufficient for melting or softening the polymer.
8. A chain extender for step-growth polycondensates, where the chain extender is present in a composition as claimed in claim 1 .
9. The chain extender as claimed in claim 8 , wherein the polycondensates are polyamides, polyesters, polycarbonates or polyurethanes.
10. The chain extender as claimed in claim 8 , wherein the compound of formula (1) is present in an amount of from 1 to 30 wt.-%, relative to the total weight of the composition and the polycondensate.
11. The chain extender as claimed in claim 8 , wherein the polycondensates are manufactured into polymeric articles.
12. The chain extender as claimed in claim 11 , wherein the polymeric articles are sheets, films, containers or fibers.
13. The method as claimed in claim 7 , wherein the let down polymer having at least one carboxyl group is a polycondensate.
14. The method as claimed in claim 13 , wherein the polycondensate is selected from the group consisting of polyamides, polyesters, polycarbonates, and polyurethanes.
15. The method as claimed in claim 7 , wherein the amount of the composition comprising at least one chain extender and at least one carrier resin which is added to the let down polymer is between 5.0 and 25 wt.-%, relative to the total weight of the composition and the let down polymer.
16. The method as claimed in claim 13 , wherein the polycondensate is manufactured into polymeric articles.
17. The method as claimed in claim 16 , wherein the polymeric articles are sheets, films, containers or fibers.