Perovskite nanocrystal particle light-emitter whose content is changed, method of producing the same, and light emitting element using the same

1. An organic/inorganic/hybrid perovskite nanocrystal particle light-emitter having a gradient structure, the light-emitter comprising an organic/inorganic/hybrid perovskite nanocrystal structure which is dispersible in an organic solvent or organic material,

wherein the nanocrystal structure has a gradient composition in which a composition is changed from the center thereof to the outside.

2. The light-emitter of claim 1 , wherein the organic solvent includes a polar solvent or a a non-polar solvent,

wherein:

the polar solvent includes dimethylformamide, gamma butyrolactone, N-methylpyrrolidone, dimethyl sulfoxide or isopropyl alcohol; and

the non-polar solvent includes dichloroethylene, trichlorethylene, chloroform, chlorobenzene, dichlorobenzene, styrene, xylene, toluene, or cyclohexene.

3. The light-emitter of claim 1 , wherein the organic/inorganic/hybrid perovskite nanocrystal particle has a spherical, cylindrical, elliptical pillar, polygonal pillar shape.

4. The light-emitter of claim 1 , wherein a size of the nanocrystal particle ranges from 1 nm to 900 nm.

5. The light-emitter of claim 1 , wherein a bandgap energy of the organic/inorganic/hybrid perovskite nanocrystal particle is determined by a crystalline structure without depending on the size of the particle.

6. The light-emitter of claim 1 , wherein the organic/inorganic/hybrid perovskite has a structure of ABX 3-h X′ h , A 2 BX 4-l X′ l , or ABX 4-k X′ k ,

wherein:

A is an organic ammonium material, B is a metal material, X is Br, X′ is Cl, h is real number of 0 to 3, and l and k are real numbers of 0 to 4; and

values of h, l, and k are increased from a center of the nanocrystal structure to the outside.

7. The light-emitter of claim 6 , wherein:

the A is (CH 3 NH 3 ) n , (C m H 2m+1 ) x NH 4-x , ((C m H 2m+1 ) y NH 3-y )(CH 2 ) z NH 3 , (CF 3 NH 3 ), (C m F 2m+1 ) x NH 4-x , ((C m F 2m+1 ) y NH 3-y )(CH 2 ) z NH 3 , (CH(NH 2 ) 2 ), (C m H 2m+1 )(C(NH 2 ) 2 ), (C m F 2m+1 )(C(NH 2 ) 2 ), metal, or a combination thereof (where n, m, x, y, and z are integers greater than 1 or equal to 1); and

the B is a bivalent transition metal, a molecule, a rare-earth metal, an alkaline-earth metal, Pb, Sn, Ge, Ga, In, Al, Sb, Bi, Po, or a combination thereof.

8. The light-emitter of claim 6 , wherein the values of h, l, and k are gradually increased from the center of the nanocrystal structure to the outside.

9. The light-emitter of claim 6 , wherein the values of h, l, and k are increased stepwise from the center of the nanocrystal structure to the outside.

10. The light-emitter of claim 1 , further comprising a plurality of organic ligands configured to surround the perovskite nanocrystal structure.

11. The light-emitter of claim 10 , wherein the organic ligands include an alkyl halide.

12. The light-emitter of claim 11 , wherein an alkyl structure of the alkyl halide includes an acyclic alkyl having a structure of C n H 2n+1 , a primary alcohol, a secondary alcohol, a tertiary alcohol, an alkylamine, p-substituted aniline, phenyl ammonium, or fluorine ammonium.

13. A light emitting element comprising:

a first electrode;

a second electrode; and

a light emitting layer, which is located between the first electrode and the second electrode and includes the organic/inorganic/hybrid perovskite nanocrystal particle light-emitter having a gradient structure according to claim 1 .

14. A method of producing an organic/inorganic/hybrid perovskite nanocrystal particle light-emitter having a gradient structure, the method comprising:

preparing an organic/inorganic/hybrid perovskite nanocrystal particle having a core-shell structure in which a composition of a core is different from a composition of a shell; and

forming the organic/inorganic/hybrid perovskite nanocrystal particle having a core-shell structure so as to have a gradient composition through interdiffusion by performing heat treatment thereon.

15. The method of claim 14 , wherein the preparing of the organic/inorganic/hybrid perovskite nanocrystal particle having a core-shell structure includes:

preparing a first solution in which a first organic/inorganic/hybrid perovskite is dissolved in a polar solvent and a second solution in which an alkyl halide surfactant is dissolved in an non-polar solvent;

forming a core including a first organic/inorganic/hybrid perovskite nanocrystal by mixing the first solution with the second solution; and

forming a shell, which includes a second organic/inorganic/hybrid perovskite nanocrystal and surrounds the core, by adding a third solution, in which a second organic/inorganic/hybrid perovskite having a larger bandgap than that of the first organic/inorganic/hybrid perovskite is dissolved, to the second solution.

16. The method of claim 15 , wherein:

the first organic/inorganic/hybrid perovskite has a structure of ABX 3 , A 2 BX 4 or ABX 4 ; and

the second organic/inorganic/hybrid perovskite has a structure of ABX′ 3 , A 2 BX′ 4 or ABX′ 4 ,

wherein A is an organic ammonium material, B is a metal material, X is Br, and X′ is Cl.

17. The method of claim 14 , wherein the preparing of the organic/inorganic/hybrid perovskite nanocrystal particle having a core-shell structure includes:

preparing a first solution in which a first organic/inorganic/hybrid perovskite is dissolved in a polar solvent and a second solution in which an alkyl halide surfactant is dissolved in an non-polar solvent;

forming a core including a first organic/inorganic/hybrid perovskite nanocrystal by mixing the first solution with the second solution; and

forming a shell, which has a larger bandgap than that of the core and surrounds the core, by adding an organic ammonium halide solution to the second solution and then stirring.

18. The method of claim 14 , wherein the preparing of the organic/inorganic/hybrid perovskite nanocrystal particle having a core-shell structure includes:

preparing a first solution in which a first organic/inorganic/hybrid perovskite is dissolved in a polar solvent and a second solution in which an alkyl halide surfactant is dissolved in an non-polar solvent;

forming a core including a first organic/inorganic/hybrid perovskite nanocrystal by mixing the first solution with the second solution;

thermally decomposing a surface of the core by performing heat treatment on the second solution; and

forming a shell, which has a larger bandgap than that of the core and surrounds the core, by adding an organic ammonium halide solution to the heat-treated second solution.

19. A method of producing an organic/inorganic/hybrid perovskite nanocrystal particle light-emitter having a gradient structure, the method comprising:

preparing a first solution in which a first organic/inorganic/hybrid perovskite is dissolved in a polar solvent and a second solution in which an alkyl halide surfactant is dissolved in an non-polar solvent;

forming a core including a first organic/inorganic/hybrid perovskite nanocrystal by mixing the first solution with the second solution; and

forming a shell, which has a larger bandgap than that of the core and surrounds the core, by adding a third solution, in which a second organic/inorganic/hybrid perovskite is dissolved, to the second solution while changing a composition of the second organic/inorganic/hybrid perovskite.

20. The method of claim 19 , wherein the second organic/inorganic/hybrid perovskite has a structure of ABX 3-h X′ h , A 2 BX 4-l X′ l , or ABX 4-k X′ k ,

wherein:

A is an organic ammonium material or metal, B is a metal or ammonium material, X is Br, and X′ is Cl, h is real number of 0 to 3, and l and k are real numbers of 0 to 4; and

the third solution, in which the second organic/inorganic/hybrid perovskite is dissolved, is added to the second solution while increasing a value of h, l, or k.

21. An inorganic metal halide perovskite nanocrystal particle light-emitter having a gradient structure, the light-emitter comprising an inorganic metal halide perovskite nanocrystal structure which is dispersible in an organic solvent,

wherein the nanocrystal structure has a gradient composition in which a composition is changed from the center thereof to the outside.

22. The light-emitter of claim 21 , wherein the inorganic metal halide perovskite has a structure of ABX 3-m X′ m , A 2 BX 4-l X′ l , or ABX 4-k X′ k ,

wherein:

A is an alkali metal, B is a metal material, X is Br, X′ is Cl, h is real number of 0 to 3, and l and k are real numbers of 0 to 4; and

values of m, l, and k are increased from a center of the nanocrystal structure to the outside.

23. The light-emitter of claim 22 , wherein:

the A is Na, K, Rb, Cs, or Fr; and

the B is a bivalent transition metal, a rare-earth metal, an alkaline-earth metal, Pb, Sn, Ge, Ga, In, Al, Sb, Bi, Po, or a combination thereof.

24. The light-emitter of claim 22 , wherein values of m, l, and k are gradually increased from the center of the nanocrystal structure to the outside.

25. The light-emitter of claim 22 , wherein values of m, l, and k are increased stepwise from the center of the nanocrystal structure to the outside.

26. The light-emitter of claim 21 , further comprising a plurality of organic or inorganic ligands configured to surround the perovskite nanocrystal structure.

27. A solar cell comprising:

a first electrode;

a second electrode; and

a photoactive layer, which is located between the first electrode and the second electrode and includes the organic/inorganic/hybrid perovskite nanocrystal particle light-emitter having a gradient structure according to claim 1 or the inorganic metal halide perovskite nanocrystal particle light-emitter having a gradient structure according to claim 21 .