Lumen stent and preform thereof, and methods for preparing lumen stent and preform thereof
A lumen stent preform is provided using a plasma nitriding technology, a preparation method thereof, a method for preparing a lumen stent by using the preform, and a lumen stent obtained according to the method. The preform is manufactured by using pure iron or an iron alloy containing no strong nitrogen compound, has a hardness of 160-250HV0.05/10, and has a microstructure that is a deformed structure having a grain size number greater than or equal to 9 or a deformed structure after cold machining. Alternatively, the preform is an iron alloy containing a strong nitrogen compound, and has a microstructure that is a deformed structure having a grain size number greater than or equal to 9 or a deformed structure after cold machining. The lumen stent preform meets the requirements of a conventional stent for radial strength and plasticity, so that plasma nitriding is applicable to commercial preparation of a lumen stent.
1. A stent, comprising a tube having an outer diameter and a lumen, the tube being formed from an iron alloy containing at least one strong nitride-forming element, a total alloy element content of the iron alloy is less than or equal to 3 wt. %, and a total content of the strong nitride-forming element is greater than or equal to 0.05 wt. %; the tube having a radial strength of at least 80 kPa; and the stent as a microstructure that has equiaxed grains having a uniform structure with a grain size number greater than or equal to 9, and wherein the strong nitride-forming element comprises at least one of Ti, Cr, Zr, Nb, V, B, W, and Mo.
2. The stent of claim 1 , wherein the total alloy elements of the iron alloy has a carbon content of less than or equal to 0.45 wt. %.
3. The stent of claim 1 , wherein the lumen stent preform has an outer diameter of 1.2-4.2 mm and a wall thickness of 0.08-0.24 mm.
4. The stent of claim 1 , wherein the stent is a coronary stent, a vascular stent, an esophageal stent, or a tracheal stent.
5. The stent of claim 1 , wherein the tube has a radial strength between 85-130 kPa.
6. The stent of claim 1 , wherein the tube has a hardness of 250-350HV0.05/10.