Coating composition comprising a binder formed from polyester and a phosphorus acid
Coating compositions that include a binder formed from a polyester and a phosphorus acid are disclosed. The binder includes a polyester material formed as the reaction product of a polyacid, a polyol, and a phosphorous acid, wherein the polyester material has a number-average molecular weight (Mn) from about 1,000 Da to 25,000 Da and a polydispersity index (Mw/Mn) of from about 1 to 10. The polyester material is present in the binder composition in amounts of more than about 10 weight percent (wt %). The coating compositions are useful for coating food and/or beverage containers.
1. A coating composition comprising a binder, the binder comprising a polyester material, wherein the polyester material comprises the reaction product of:
a polyester prepolymer formed by reaction of (a) a polyacid and (b) a polyol; and
a phosphorous acid,
wherein the polyester material has a number-average molecular weight (Mn) from about 5, 000 Da to 25,000 Da, a polydispersity index (Mw/Mn) of from about 1 to 10 and is present in said binder in amounts of more than about 10 weight percent (wt %).
2. The coating composition according to claim 1 , wherein the polyacid comprises terephthalic acid, isophthalic acid, maleic anhydride, itaconic acid, 1,4-cyclohexane dicarboxylic acid, adipic acid, succinic acid, succinic anhydride, sebacic acid or a combination thereof.
3. The coating composition according to claim 2 , wherein the polyacid comprises terephthalic acid, isophthalic acid, 1,4-cyclohexane dicarboxylic acid, maleic anhydride, itaconic acid or a combination thereof.
4. The coating composition according to claim 2 , wherein the polyacid comprises 1,4-cyclohexane dicarboxylic acid, terephthalic acid, isophthalic acid, adipic acid, succinic acid, succinic anhydride, sebacic acid or a combination thereof.
5. The coating composition according to claim 1 , wherein the polyol comprises ethylene glycol, 2-methyl-1,3-propanediol, 1, 2 propanediol, cyclohexanedimethanol (CHDM), trimethylol propane or glycerol or a combination thereof.
6. The coating composition according to claim 1 , wherein the phosphorous acid comprises phosphoric acid.
7. The coating composition according to claim 1 , wherein the molar ratio of (a):(b) ranges from 5:1 to 1:5.
8. The coating composition according to claim 1 , wherein the phosphorous acid is provided in amounts from 0.1 to 1.0 equivalents of phosphorous acid per hydroxyl equivalent of the polyester material.
9. The coating composition according to claim 1 , wherein the polyester material has a weight-average molecular weight (Mw) from 1,500 Da to about 300,000 Da.
10. The coating composition according to claim 1 , wherein the coating composition further comprises a crosslinking agent.
11. A coating composition comprising a binder, the binder comprising a polyester material, wherein the polyester material comprises the reaction product of a two step process, the two step process comprising:
a first step comprising preparing a polyester prepolymer by contacting
(a) a polyacid,
(b) a polyol, and
a second step comprising contacting the polyester prepolymer with
(c) a phosphorous acid,
wherein the polyester material has a number-average molecular weight (Mn) from about 2,000 Da to 25,000 Da, a polydispersity index (Mw/Mn) of from about 1 to 10 and is present in said binder in amounts of more than about 10 weight percent (wt %).
12. The coating composition according to claim 11 , wherein reaction conditions of the first step include a temperature of between 100° C. and 250° C.
13. The coating composition according to claim 12 , reaction conditions of the second step include a temperature of between 90° C. and 200° C.
14. The coating composition according to claim 11 , wherein the polydispersity index of the polyester material is from 0 to 5 units higher than the polydispersity index of the polyester prepolymer.
15. A coated article coated on at least a portion thereof with a coating composition according to claim 1 .
16. A food or beverage container coated on at least a portion thereof with a coating composition according to claim 1 .
17. A coated article coated on at least a portion thereof with a coating composition according to claim 11 .
18. A food or beverage container coated on at least a portion thereof with a coating composition according to claim 11 .