Preform for biaxial stretching blow molding, and container
A preform for biaxial stretching blow molding. The preform being formed into a closed-end cylinder by direct blow molding and which is to be shaped into a container using a pressurizing liquid medium. The preform has either a single-layer or a multilayer structure constituted of one of a polyethylene resin having an MFR of 1.0-1.5 g/10 min. or a polypropylene resin having an MFR of 0.8 to 2.3 g/10 min.
1. A preform shaped by direct blow molding for biaxial stretching blow molding into a container using a pressurizing liquid medium, the preform comprising:
a closed end generally cylindrical body having a multilayer structure with at least one layer of a polyethylene resin having an MFR of 1.0 to 1.5 g/10 min., the multilayer structure having an inner layer configured of an ethylene vinyl alcohol copolymer resin inside an outer layer configured of the polyethylene resin; and
a band shaped adhesive layer configured of a modified polyolefin resin and extending in the axial direction between the outer layer and the inner layer.
2. The preform according to claim 1 , comprising an innermost layer configured of a modified polyolefin resin inside the inner layer.
3. The preform according to claim 1 , further comprising a cross shaped parting line at a bottom part of the closed end generally cylindrical body.
4. A container shaped by biaxial stretching blow molding using a liquid pressurizing medium with the preform according to claim 3 .
5. A preform shaped by direct blow molding for biaxial stretching blow molding into a container using a pressurizing liquid medium, the preform comprising:
a closed end generally cylindrical body having at least one layer thereof being constituted of one of a polyethylene resin having an MFR of 1.0 to 1.5 g/10 min. and polypropylene resin having an MFR of 0.8 to 2.3 g/10 min.;
the body having an inner layer configured of an ethylene vinyl alcohol copolymer resin inside an outer layer of the one the polyethylene resin and polypropylene resin; and
an innermost layer configured of a modified polyolefin resin inside the inner layer.
6. The preform according to claim 5 , comprising a cross shaped parting line at the bottom part.
7. A method of forming a container from a preform, the method comprising:
extruding a resin tube structure, the resin being one of a polyethylene resin having an MFR of 1.0 to 1.5 g/10 min. and polypropylene resin having an MFR of 0.8 to 2.3 g/10 min.;
forming a preform from the tube structure by direct blow molding using pressurized air as the blowing medium, the preform having a closed end generally cylindrical body;
forming a container from the preform by biaxial stretching blow molding the preform into the container using a pressurizing liquid as the blowing medium; and
the extruding step including extruding the tube structure as multilayer structure, wherein the multilayer structure an inner layer configured of an ethylene vinyl alcohol copolymer resin inside an outer layer configured of one of the polyethylene resin and the polypropylene resin, the multilayer structure further including a band shaped adhesive layer configured of a modified polyolefin resin and extending in the axial direction between the outer layer and the inner layer.
8. The method according to claim 7 , wherein the multilayer structure has an innermost layer configured of a modified polyolefin resin.
9. The method according to claim 7 , further comprising the step of forming a cross shaped parting line at a bottom part of the closed end generally cylindrical body.