POLYARYLENE SULFIDE COMPOSITION WITH EXCELLENT ADHESION TO METAL
The present invention relates to a polyarylene sulfide resin composition with a low out-gas content, comprising: a polyarylene sulfide; and a phenoxy resin. The polyarylene sulfide resin composition of the present invention exhibits a low out-gas content and excellent tensile strength and metal adhesive strength, and thus can be useful as a resin composition for preparing a product requiring molding precision.
1 . A resin composition comprising a polyarylene sulfide; and a phenoxy resin of Formula 1, wherein the amount of outgassing is 300 ppm or less:
wherein n is an integer of 100 to 900.
2 . The composition of claim 1 , wherein the phenoxy resin is comprised in an amount of 0.5 to 10% by weight based on the total amount of the composition.
3 . The composition of claim 1 , further comprising a component selected from the group consisting of an elastomer, a filler, a shock absorber, an adhesiveness enhancer, a stabilizer, a pigment, and combinations thereof.
4 . The composition of claim 3 , wherein the elastomer is a thermoplastic elastomer selected from the group consisting of polyvinyl chloride elastomers, polyolefin elastomers, polyurethane elastomers, polyester elastomers, polyamide elastomers, polybutadiene elastomers, a terpolymer of glycidyl methacrylate and methyl acryl ester, and combinations thereof.
5 . The composition of claim 3 , wherein the filler is at least one organic or inorganic filler selected from the group consisting of a glass fiber, a carbon fiber, a boron fiber, a glass bead, a glass flake, talc and calcium carbonate.
6 . The composition of claim 5 , wherein the glass fiber is selected from the group consisting of an epoxy silane treated glass fiber, an amino silane treated glass fiber, and combinations thereof.
7 . The composition of claim 3 , wherein the pigment is an organic or inorganic pigment selected from the group consisting of titanium dioxide (TiO 2 ), carbon black, and combinations thereof.
8 . The composition of claim 3 , wherein the pigment is comprised in an amount of 0.1 to 10% by weight based on the total amount of the composition.
9 . The composition of claim 1 , wherein the composition has a tensile strength of 50 to 160 MPa as measured according to ASTM D 638.
10 . The composition of claim 1 , wherein the composition has an adhesive strength to metals of 25 to 75 MPa as measured according to ASTM D 3163.
11 . The composition of claim 1 , wherein the composition has an impact strength of 6.5 to 9 KJ/m 2 as measured according to ISO 179.
12 . The composition of claim 1 , wherein the composition has a chloride content of 300 ppm or less.
13 . The composition of claim 12 , wherein the composition has a chloride content of 100 ppm or less.
14 . The composition of claim 1 , wherein the polyarylene sulfide has a weight ratio of arylene sulfide repeating unit to arylene disulfide repeating unit ranging from 1:0.0001 to 1:0.5.