Polyarylene sulfide composition having excellent adhesiveness with metal
The present invention relates to a polyarylene sulfide resin composition with a low outgas content, the composition containing: a polyarylene sulfide and a silane-modified epoxy resin. The polyarylene sulfide resin composition of the present invention shows excellent tensile strength and metal bonding strength as well as a low outgas content, and thus can be favorably used as a resin composition for manufacturing a product requiring molding accuracy.
1. A resin composition comprising a polyarylene sulfide; and a silane-modified epoxy resin of Formula 1, wherein the amount of outgassing is 300 ppm or less:
wherein
R 1 is hydrogen or C 1-6 alkyl;
R 2 is selected from the group consisting of epoxy, amino, mercapto, vinyl, and combinations thereof; and
n is an integer of 1 to 100.
2. The composition of claim 1 , wherein the silane-modified epoxy resin is comprised in an amount of 0.5 to 10% by weight based on the total amount of the composition.
3. The composition of claim 1 , further comprising a component selected from the group consisting of an elastomer, a filler, a shock absorber, an adhesiveness enhancer, a stabilizer, a pigment, and combinations thereof.
4. The composition of claim 3 , wherein the elastomer is a thermoplastic elastomer selected from the group consisting of polyvinyl chloride elastomers, polyolefin elastomers, polyurethane elastomers, polyester elastomers, polyamide elastomers, polybutadiene elastomers, a terpolymer of glycidyl methacrylate and methyl acryl ester, and combinations thereof.
5. The composition of claim 3 , wherein the filler is at least one organic or inorganic filler selected from the group consisting of a glass fiber, a carbon fiber, a boron fiber, a glass bead, a glass flake, talc, and calcium carbonate.
6. The composition of claim 5 , wherein the glass fiber is selected from the group consisting of a urethane/epoxy silane treated glass fiber, a urethane/amino silane treated glass fiber, and combinations thereof.
7. The composition of claim 3 , wherein the pigment is an organic or inorganic pigment selected from the group consisting of titanium dioxide (TiO 2 ), carbon black, and combinations thereof.
8. The composition of claim 3 , wherein the pigment is comprised in an amount of 0.1 to 10% by weight based on the total amount of the composition.
9. The composition of claim 1 , wherein the composition has a tensile strength of 50 to 150 MPa as measured according to ASTM D 638.
10. The composition of claim 1 , wherein the composition has an adhesive strength to metals of 25 MPa or higher as measured according to ASTM D 3163.