Provided is a Ni-based alloy having a composition consisting of, by mass %, Cr: 14.0% to 17.0% (preferably, not less than 14.0% and less than 15.0%), Fe: 5.0% to 9.0%, Ti: 2.2% to 2.8%, Al: 0.40% to 1.00%, a total amount of Nb+Ta: 0.7% to 1.2%, B: 0.001% to 0.010%, Zr: 0.01% to 0.15%, Mg: 0.001% to 0.050%, Mn: 0.01% to 0.20%, Cu: 0.005% to 0.300%, Mo: 0.01% to 0.30%, C: 0.01% to 0.05%, and the balance of Ni with inevitable impurities. In a creep test under conditions of a test temperature of 750° C. and a test load of 330 MPa, the Ni-based alloy preferably has a creep rupture life of not less than 120 hours and an elongation of not less than 16%, i.e., has good high-temperature creep characteristics. The Ni-based alloy is suitable for a gas turbine member.
1. An Ni-based alloy having a composition consisting of, by mass %, Cr: 14.0% to 17.0%, Fe: 5.0% to 9.0%, Ti: 2.2% to 2.8%, Al: 0.40% to 1.00%, a total amount of Nb+Ta: 0.7% to 1.2%, B: 0.001% to 0.010%, Zr: 0.01% to 0.15%, Mg: 0.001% to 0.050%, Mn: 0.01% to 0.20%, Cu: 0.005% to 0.300%, Mo: 0.01% to 0.30%, C: 0.01% to 0.05%, and the balance of Ni with inevitable impurities.
2. The Ni-based alloy according to claim 1 , wherein a total content of B, Zr, Cu, and Mo is from 0.18% to 0.51%.
3. The Ni-based alloy according to claim 1 , wherein the content of Cr is not less than 14.0% and less than 15.0%.
4. The Ni-based alloy according to claim 1 , wherein in a creep test under conditions of a test temperature of 750° C. and a test load of 330 MPa, the Ni-based alloy has a creep rupture life of at least 120 hours and an elongation of at least 16%.
5. A gas turbine member, comprising the Ni-based alloy according to claim 1 .