IMPELLER FOR ROTARY MACHINE, COMPRESSOR, SUPERCHARGER, AND METHOD FOR PRODUCING IMPELLER FOR ROTARY MACHINE
An impeller for a rotary machine includes: a base material of the impeller comprising Al or an Al alloy; and an electroless plating layer disposed so as to cover the base material, the electroless plating layer forming a surface layer of the impeller. The electroless plating layer comprises a Ni—P based alloy having an amorphous structure, the Ni—P based alloy having a P content rate of not less than 5 wt % and not more than 11 wt % in the electroless plating layer.
1 . An impeller for a rotary machine, comprising:
a base material of the impeller comprising Al or an Al alloy; and
an electroless plating layer disposed so as to cover the base material, the electroless plating layer forming a surface layer of the impeller,
wherein the electroless plating layer comprises a Ni—P based alloy having an amorphous structure, the Ni—P based alloy having a P content rate of not less than 5 wt % and not more than 11 wt % in the electroless plating layer.
2 . The impeller for a rotary machine according to claim 1 ,
wherein the electroless plating layer has a layer thickness of not less than 15 μm and not more than 60 μm.
3 . The impeller for a rotary machine according to claim 1 ,
wherein the electroless plating layer has a Vickers hardness of not less than 500 HV and not more than 700 HV.
4 . The impeller for a rotary machine according to claim 1 ,
wherein a fracture ductility strain of the electroless plating layer is not less than 0.5%.
5 . The impeller for a rotary machine according to claim 1 ,
wherein the impeller is a compressor impeller of a supercharger.
6 . A compressor comprising a compressor impeller which comprises the impeller according to claim 1 .
7 . A supercharger, comprising:
the compressor according to claim 6 ; and
a turbine for driving the compressor.
8 . The supercharger according to claim 7 ,
wherein the compressor is disposed in an intake passage of an internal combustion engine,
wherein the turbine is configured to be driven by exhaust gas from the internal combustion engine, and
wherein a part of the exhaust gas is circulated to the intake passage at an upstream side of the compressor.
9 . A method of producing an impeller for a rotary machine, comprising:
a step of forming an electroless plating layer as a surface layer of the impeller comprising Al or an Al alloy, so as to cover a base material of the impeller,
wherein the electroless plating layer comprises a Ni—P based alloy having an amorphous structure, the Ni—P based alloy having a P content rate of not less than 5 wt % and not more than 11 wt % in the electroless plating layer.
10 . The method of producing an impeller for a rotary machine according to claim 9 , further comprising a step of cutting out a test piece from the impeller on which the electroless plating layer is formed, and using the test piece to evaluate a fracture ductility of the electroless plating layer.
11 . The method of producing an impeller for a rotary machine according to claim 10 , wherein the test piece is collected from a region on a back surface of the hub of the impeller, the region being a projection of a blade root portion of the hub on the back surface of the hub.
12 . The method of producing an impeller for a rotary machine according to claim 10 , further comprising a step of changing a plating condition of the electroless plating layer if the fracture ductility is smaller than a threshold.