Chemical heat storage material, and composition for forming chemical heat storage material
The purpose of the present invention is to provide: a chemical heat storage material which may be molded into an article having high strength and high heat conductivity; and a composition for forming a chemical heat storage material, whereby it becomes possible to mold the chemical heat storage material in a desired shape. A chemical heat storage material comprising a Group-2 element compound, a boron compound and a silicone polymer; and a composition for forming a chemical heat storage material, said composition comprising a Group-2 element compound, a boron-containing compound, at least one component selected from the group consisting of an alkoxysilane, a hydrolysate of the alkoxysilane and a condensation product of the alkoxysilane, and a resin.
1. A chemical heat storage material obtained by calcining the composition comprising:
a Group-2 element compound of at least one selected from the group consisting of calcium hydroxide, and magnesium hydroxide,
trimethyl borate, and
a low condensate of ethyl silicate at 200 to 1200° C.,
wherein the Group-2 element compound is calcium hydroxide and the contents of calcium atoms, boron atoms and silicon atoms in the chemical heat storage material are 13 to 59% by mass, 0.4 to 11.3% by mass and 4.8 to 33.2% by mass, respectively,
wherein the Group-2 element compound is magnesium hydroxide and the contents of magnesium atoms, boron atoms and silicon atoms in the chemical heat storage material are 8.3 to 46.5% by mass, 0.5 to 11.9% by mass and 6.2 to 35.1% by mass, respectively.
2. A composition for forming the chemical heat storage material according to claim 1 , comprising:
a Group-2 element compound of at least one selected from the group consisting of calcium hydroxide, and magnesium hydroxide,
trimethyl borate,
a low condensate of ethyl silicate, and
at least one selected from the group consisting of
polyethylene glycol and butyral resin.
3. The composition for forming a chemical heat storage material according to claim 2 , further comprising glass fiber.
4. A method for producing a chemical heat storage material, comprising the steps of
coating a metal substrate surface with a composition for forming a chemical heat storage material according to claim 2 ; and
calcining the composition for forming a chemical heat storage material on the metal substrate surface at 200 to 1200° C. for 30 to 120 minutes after the coating step.