Polycarbonate resin composition and molded body of same

1. A polycarbonate-based resin composition, comprising a polycarbonate-based resin containing a polycarbonate-polyorganosiloxane copolymer (E-1), and 0.01 to 1.0 part by mass of a UV absorber (C) with respect to 100 parts by mass of the polycarbonate-based resin, wherein:

the polycarbonate-polyorganosiloxane copolymer (E-1) has a polycarbonate block (A) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (B) containing a repeating unit represented by the following general formula (II) wherein the polyorganosiloxane block (B) has an average chain length of 40 to 85; and

in a differential molecular weight distribution curve obtained from measurement of the polyorganosiloxane block (B) by gel permeation chromatography (GPC) using a polystyrene calibration curve, the curve having an axis of abscissa indicating a logarithmic value log(M) of a molecular weight M and an axis of ordinate indicating dw/d log(M) obtained by differentiating a concentration fraction w with respect to the logarithmic value log(M) of the molecular weight,

(1) a dw/d log(M) value becomes maximum in a range of 3.4≤log(M)≤4.0, and

(2) a ratio of a value obtained by integrating the dw/d log(M) value over a range of 4.00≤log(M)≤4.50 to a value obtained by integrating the dw/d log(M) value over an entire range of the log(M) in the differential molecular weight distribution curve is 6.5 to 40%;

a total light transmittance of a molded body, having a thickness of 3 mm, of the polycarbonate-based resin composition is 86% or more, as determined in conformity with ISO 13468:

wherein R 1 and R 2 each independently represent, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO 2 —, —O—, or —CO—, R 3 and R 4 each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and a and b each independently represent an integer of 0 to 4,

wherein the GPC has been measured with the following parameters:

(i) solvent is THE,

(ii) a column temperature of 40° C.,

(iii) a flow rate of 1.0 ml/min,

(iv) an RI Detector,

(v) an injection concentration of 0.1 w/v %,

(vi) an injection amount of 0.1 ml, and

(vii) the GPC comprises a first column and a second column, each having a length of 30 cm respectively, with a different pore size, the first column's packing material pore size is 20 nm and the second column's packing material pore size is 2 nm, and each of which has a packing material has the following conditions: particle matrix is polystyrene divinylbenzene (PS-DVB), particle size is 5 μm.

2. A polycarbonate-based resin composition, comprising a polycarbonate-based resin containing a polycarbonate-polyorganosiloxane copolymer (E-1), and 0.01 to 1.0 part by mass of a UV absorber (C) with respect to 100 parts by mass of the polycarbonate-based resin, wherein:

the polycarbonate-polyorganosiloxane copolymer (E-1) has a polycarbonate block (A) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (B) containing a repeating unit represented by the following general formula (II) wherein the polyorganosiloxane block (B) has an average chain length of 40 to 85; and

the polycarbonate-based resin composition uses, as a raw material, a polyorganosiloxane having the following features: in a differential molecular weight distribution curve obtained from measurement by gel permeation chromatography (GPC) using a polystyrene calibration curve, the curve having an axis of abscissa indicating a logarithmic value log(M) of a molecular weight M and an axis of ordinate indicating dw/d log(M) obtained by differentiating a concentration fraction w with respect to the logarithmic value log(M) of the molecular weight,

(1) a dw/d log(M) value becomes maximum in a range of 3.4≤log(M)≤4.0, and

(2) a ratio of a value obtained by integrating the dw/d log(M) value over a range of 4.00≤log(M)≤4.50 to a value obtained by integrating the dw/d log(M) value over an entire range of the log(M) in the differential molecular weight distribution curve is 6.5 to 40%;

a total light transmittance of a molded body, having a thickness of 3 mm, of the polycarbonate-based resin composition is 86% or more, as determined in conformity with ISO 13468:

wherein R 1 and R 2 each independently represent, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO 2 —, —O—, or —CO—, R 3 and R 4 each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and a and b each independently represent an integer of 0 to 4,

wherein the GPC has been measured with the following parameters:

(i) solvent is THE,

(ii) a column temperature of 40° C.,

(iii) a flow rate of 1.0 ml/min,

(iv) an RI Detector,

(v) an injection concentration of 0.1 w/v %,

(vi) an injection amount of 0.1 ml, and

(vii) the GPC comprises a first column and a second column, each having a length of 30 cm respectively, with a different pore size, the first column's packing material pore size is 20 nm and the second column's packing material pore size is 2 nm, and each of which has a packing material has the following conditions: particle matrix is polystyrene divinylbenzene (PS-DVB), particle size is 5 μm.

3. A polycarbonate-based resin composition, comprising a polycarbonate-based resin containing a polycarbonate-polyorganosiloxane copolymer, and 0.01 to 1.0 part by mass of a UV absorber (C) with respect to 100 parts by mass of the polycarbonate-based resin, wherein:

the polycarbonate-polyorganosiloxane copolymer comprises a polycarbonate-polyorganosiloxane copolymer (E′-1) having a polycarbonate block (A′) formed of a repeating unit represented by the following general formula (I) and a polyorganosiloxane block (B′) containing a repeating unit represented by the following general formula (II) wherein the polyorganosiloxane block (B′) has an average chain length of 40 to 85;

in a differential molecular weight distribution curve obtained from measurement of the polyorganosiloxane block (B′) by gel permeation chromatography (GPC) using a polystyrene calibration curve, the curve having an axis of abscissa indicating a logarithmic value log(M) of a molecular weight M and an axis of ordinate indicating dw/d log(M) obtained by differentiating a concentration fraction w with respect to the logarithmic value log(M) of the molecular weight,

(1) a dw/d log(M) value becomes maximum in a range of 3.4≤log(M)≤4.0,

(2) a ratio of a value obtained by integrating the dw/d log(M) value over a range of 4.00≤log(M)≤4.50 to a value obtained by integrating the dw/d log(M) value over an entire range of the log(M) in the differential molecular weight distribution curve is 6.5 to 40%;

a total light transmittance of a molded body, as determined in conformity with ISO 13468, having a thickness of 3 mm, of the polycarbonate-based resin composition is 85% or more;

a viscosity-average molecular weight of the polycarbonate-polyorganosiloxane copolymer (E′-1) is 14,000 to 22,000 as calculated from Schnell's equation: [η]=1.23×10 −5 ×Mv 0.83 by using a limiting viscosity [η] determined through the measurement of viscosity of a methylene chloride solution at 20° C. with an Ubbelohde-type viscometer; and

an Izod impact strength, as determined using notched test piece having a thickness of 3.2 mm in conformity with ASTM Standard D-256, of the composition at −40° C. is 40 kJ/m 2 or more:

wherein R 1 and R 2 each independently represent, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO 2 —, —O—, or —CO—, R 3 and R 4 each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and a and b each independently represent an integer of 0 to 4,

wherein the GPC has been measured with the following parameters:

(i) solvent is THE,

(ii) a column temperature of 40° C.,

(iii) a flow rate of 1.0 ml/min,

(iv) an RI Detector,

(v) an injection concentration of 0.1 w/v %,

(vi) an injection amount of 0.1 ml, and

(vii) the GPC comprises a first column and a second column, each having a length of 30 cm respectively, with a different pore size, the first column's packing material pore size is 20 nm and the second column's packing material pore size is 2 nm, and each of which has a packing material has the following conditions: particle matrix is polystyrene divinylbenzene (PS-DVB), particle size is 5 μm.

4. The polycarbonate-based resin composition according to claim 1 , wherein a content of the polyorganosiloxane block (B) in the polycarbonate-polyorganosiloxane copolymer (E-1)) is 0.5 to 20.0 mass %.

5. The polycarbonate-based resin composition according to claim 1 , wherein the polycarbonate-polyorganosiloxane copolymer (E-1) has a viscosity-average molecular weight of 14,000 to 22,000, as calculated from Schnell's equation: [η]=1.23×10 −5 ×Mv 0.83 by using a limiting viscosity [η] determined through the measurement of viscosity of a methylene chloride solution at 20° C. with an Ubbelohde-type viscometer.

6. The polycarbonate-based resin composition according to claim 1 , wherein the UV absorber (C) comprises at least one selected from a benzoxazinone-based UV absorber, a benzotriazole-based UV absorber, a salicylate-based UV absorber, a malonic acid ester-based UV absorber, an oxalylanilide-based UV absorber, a triazine-based UV absorber, a benzophenone-based UV absorber, and a cyanoacrylate-based UV absorber.

7. The polycarbonate-based resin composition according to claim 6 , wherein the UV absorber (C) comprises at least one selected from the benzoxazinone-based UV absorber and the benzotriazole-based UV absorber.

8. The polycarbonate-based resin composition according to claim 1 , wherein in the general formula (I), a and b each represent 0, and X represents a single bond or an alkylidene group having 2 to 8 carbon atoms.

9. The polycarbonate-based resin composition according to claim 8 , wherein in the general formula (I), a and b each represent 0, and X represents an alkylidene group having 3 carbon atoms.

10. The polycarbonate-based resin composition according to claim 1 , wherein in the general formula (II), R 3 and R 4 each represent a methyl group.

11. A molded body, which is obtained by molding the polycarbonate-based resin composition of claim 1 .

12. The molded body according to claim 11 , wherein the molded body comprises a part for electrical and electronic equipment.

13. The polycarbonate-based resin composition according to claim 3 , wherein a content of the polyorganosiloxane block (B′) in the polycarbonate-polyorganosiloxane copolymer (E′-1) is 0.5 to 20.0 mass %.

14. The polycarbonate-based resin composition according to claim 1 , wherein the average chain length of the polyorganosiloxane block (B) in the polycarbonate-polyorganosiloxane copolymer (E-1) is 58 to 85.

15. The polycarbonate-based resin composition according to claim 1 , wherein a content of the polyorganosiloxane block (B) in the polycarbonate-polyorganosiloxane copolymer (E-1) is 1.5 to 6.0 mass %.

16. The polycarbonate-based resin composition according to claim 3 , wherein the average chain length of the polyorganosiloxane block (B′) in the polycarbonate-polyorganosiloxane copolymer (E′-1) is 58 to 85.

17. The polycarbonate-based resin composition according to claim 3 , wherein a content of the polyorganosiloxane block (B′) in the polycarbonate-polyorganosiloxane copolymer (E′-1) is 1.5 to 6.0 mass %.