Method for producing particulate water-absorbing agent
Provided is a method for producing a particulate water absorbing agent, the method including the steps of: a polymerization step of polymerizing an acrylic acid (salt)-based aqueous monomer solution so as to obtain a crosslinked hydrogel polymer; a drying step of drying the crosslinked hydrogel polymer so as to obtain a dried polymer; a classification step of classifying a polymer subjected to classification so as to obtain a water-absorbing resin powder having a specific particle size; and a surface-crosslinking step of surface-crosslinking the water-absorbing resin powder that is not surface crosslinked, wherein the classification step is carried out at least either or both of before and/or after the surface-crosslinking step but after said drying step, and wherein a hole shape of a classification sieve used in the classification step is an irregular polygonal or non-circular.
1. A method for producing a particulate water absorbing agent containing a polyacrylic acid (salt)-based water-absorbing resin as a main component, the method comprising:
a polymerization step of polymerizing an acrylic acid (salt)-based aqueous monomer solution so as to obtain a crosslinked hydrogel polymer;
a drying step of drying said crosslinked hydrogel polymer so as to obtain a dried polymer;
a classification step of classifying a polymer subjected to classification; and
a surface-crosslinking step of surface-crosslinking an unsurface-crosslinked water-absorbing resin powder,
wherein the classification step is carried out at least either or both of before and/or after the surface-crosslinking step but after said drying step, and
wherein a hole shape of a classification sieve used in the classification step is irregular polygonal or non-circular.
2. The method according to claim 1 , wherein the hole shape of the classification sieve is rectangular or oval.
3. The method according to claim 1 , wherein the classification step is carried out after the surface-crosslinking step.
4. The method according to claim 1 , wherein a ratio of length of a major axis to a minor axis of a hole of the classification sieve is not less than 1.2.
5. The method according to claim 1 , wherein a fluid retention capacity under pressure (AAP) of the polymer subjected to classification that is supplied in the classification step is not less than 20 g/g.
6. The method according to claim 1 , wherein a bulk specific gravity of the polymer subjected to classification that is supplied in the classification step is not less than 0.50 g/cm3.
7. The method according to claim 1 , wherein not less than 50 weight % of the polymer subjected to classification that is supplied in the classification step has a particle diameter of less than 600 μm.
8. The method according to claim 1 , wherein the classification sieve has a metal sieve mesh whose wire diameter and shape are different.
9. The method according to claim 8 , wherein the metal sieve mesh is made of a round wire and/or a flat wire.
10. The method according to claim 1 , wherein the classification step is performed by a classification apparatus, which is an oscillating classification apparatus.
11. The method according to claim 1 , wherein the crosslinked hydrogel polymer is obtained through droplet polymerization in a vapor phase or in an organic phase.
12. The method according to claim 1 , further comprising a step of adding a classification aid to:
the polymer subjected to classification that is supplied in the classification step; and/or
the water-absorbing resin powder obtained in the classification step.
13. The method according to claim 1 , wherein a temperature of the polymer subjected to classification that is supplied in the classification step is 40° C. to 100° C.
14. The method according to claim 10 , wherein a temperature of the classification apparatus used in the classification step is set at 40° C. to 80° C.
15. The method according to claim 1 , wherein, in the classification step, the classification sieve having a hole shape of irregular polygons or non-circles is used to classify a water-absorbing resin after the drying step so as to remove coarse particles.
16. The method according to claim 15 , wherein the classification sieve whose hole has a minor-axis mesh size of 600 μm to 1000 μm is used to remove the coarse particles.
17. The method according to claim 1 ,
wherein, in the classification step, the classification sieve having a hole shape of irregular polygons or non-circles is used to classify a water-absorbing resin after the drying step so as to remove fine particles; and
wherein a hole of the classification sieve has a minor-axis mesh size of 45 μm to 300 μm.
18. The method according to claim 10 , wherein classification is performed with a temperature inside the classification apparatus or a temperature of the classification sieve being 40° C. to 120° C., and/or with an atmospheric dew point being not more than 40° C.
19. The method according to claim 1 , wherein, on condition that classification is performed multiple times before or after surface-crosslinking, the classification sieve having a hole shape of irregular polygons or non-circles is used either once or multiple times in the first, third and subsequent classifications.
20. The method according to claim 1 , wherein the classification step using the classification sieve having a hole shape of irregular polygons or non-circles is carried out for a water-absorbing resin, except for the water-absorbing resin defined below:
a water-absorbing resin remaining on a sieve used to classify a surface-crosslinked water-absorbing resin, said sieve having a smallest mesh size out of at least two kinds of sieves that are used for classification, each of which has a mesh size ranging from not less than 150 μm to not more than 850 μm.