Coating composition, method for producing same, coating film, exhaust fan and air conditioner
Provided is a coating composition containing: water; a water-soluble organic solvent that has a flash pint of at least 80° C. and not more than 200° C. and dissolves a fluorine resin; a fluorine resin; hydrophilic silica particles; and hydrophobic silica particles. The hydrophilic silica particles are preferably contained in the coating composition in an amount of at least 0.001 mass % and not more than 1 mass %. The average particle diameter of the hydrophilic silica particles is preferably at least 5 nm and not more than 30 nm.
1. A coating film formed from a coating composition comprising:
water;
a water-soluble organic solvent that has a flash point of at least 80° C. and not more than 200° C. and dissolves a fluorine resin;
a fluorine resin;
hydrophilic silica particles; and
hydrophobic silica particles,
wherein a thickness of the coating film is at least 0.2 μm and not more than 3.0 μm.
2. The coating film formed from the coating composition of claim 1 , wherein a static contact angle of the surface of the coating film with water is at least 140° and not more than 170°.
3. A coating film, comprising:
a layer in which hydrophilic silica particles are agglomerated on the surface of a substrate;
hydrophobic silica particles dispersed and arranged on the layer in which the hydrophilic silica particles are aggregate; and
a fluorine resin covering the layer in which the hydrophilic silica particles are aggregated and the hydrophobic silica particles.
4. The coating film of claim 1 , wherein the hydrophilic silica particles are contained in an amount of at least 0.001 mass % and not more than 1 mass % of the coating composition.
5. The coating film of claim 1 , wherein an average particle diameter of the hydrophilic silica particles is at least 5 nm and not more than 30 nm.
6. The coating film of claim 1 , wherein water is contained in an amount of at least 1 mass % and not more than 30 mass % of the coating composition used to form the coating film.
7. The coating film of claim 1 , wherein the coating composition used to form the coating film further comprises flat fine particles that form a card house-like aggregate structure.