Rubber composition and pneumatic tire
Provided are a rubber composition that achieves a balanced improvement in grip performance during the initial to late phases of running and abrasion resistance, and a pneumatic tire formed from the rubber composition. The present invention relates to a rubber composition containing a rubber component, sulfur, and a molten mixture of a solid resin and a plasticizer, the solid resin having an SP value of 9.2 to 13 and/or a softening point of 130° C. or higher, the plasticizer including at least one compound selected from the group consisting of phosphoric acid esters, phthalic acid esters, aliphatic polybasic acid esters, trimellitic acid esters, acetic acid esters, and ricinoleic acid esters, the solid resin being present in an amount of 1 part by mass or more per 100 parts by mass of the rubber component.
1. A method for producing a rubber composition, the method comprising:
a melting step including preparing a molten mixture of a solid resin and a plasticizer;
a base kneading step including kneading the molten mixture with a rubber component to prepare a kneaded mixture; and
a final kneading step including kneading the kneaded mixture with a sulfur to obtain said rubber composition,
wherein the solid resin has at least one of an SP value of 10.5 to 11.9 or a softening point of 140 to 160° C.,
the plasticizer includes at least one compound selected from the group consisting of phosphoric acid esters, phthalic acid esters, aliphatic polybasic acid esters, trimellitic acid esters, acetic acid esters, and ricinoleic acid esters,
wherein the plasticizer has a flash point of 200° C. or higher, and
the compound has a freezing point of −30 to −19° C., and
the solid resin is present in an amount of 1 part by mass or more per 100 parts by mass of the rubber component.
2. The method for producing the rubber composition according to claim 1 ,
wherein the compound has an SP value of 8.3 to 9.5.
3. The method for producing the rubber composition according to claim 1 ,
wherein the solid resin is an acrylic resin having an SP value of 10.5 to 11.9.
4. The method for producing the rubber composition according to claim 1 ,
wherein the plasticizer includes an aliphatic polybasic acid ester.
5. The method for producing the rubber composition according to claim 4 ,
wherein the aliphatic polybasic acid ester is bis[2-(2-butoxyethoxy)ethyl] adipate.
6. The method for producing the rubber composition according to claim 1 ,
wherein the rubber composition is a rubber composition for treads or a rubber composition for footwear soles.
7. A method for producing a pneumatic tire, the method comprising a forming step including forming a tread from the rubber composition obtained by the method for producing the rubber composition according to claim 1 .