Foam ink composition and 3D printed hierarchical porous structure
A foam ink composition for printing porous structures comprises stabilizing particles and gas bubbles dispersed in a solvent. The stabilizing particles comprise a predetermined interfacial energy so as to exhibit a contact angle with the solvent of from about 15° to about 90°. At least a portion of the stabilizing particles are positioned at interfacial regions between the solvent and the gas bubbles, thereby stabilizing the gas bubbles in the foam ink composition. A 3D printed hierarchical porous structure comprises one or more continuous filaments arranged in a predetermined pattern on a substrate, the one or more continuous filaments comprising a sintered material and including a porosity of at least about 40 vol. %.
1. A method of printing a porous structure, the method comprising:
extruding a foam ink composition through a nozzle, the foam ink composition comprising stabilizing particles and gas bubbles dispersed in a solvent, the stabilizing particles comprising a predetermined interfacial energy so as to exhibit a contact angle with the solvent of from about 15° to about 90°, and at least a portion of the stabilizing particles being positioned at interfacial regions between the solvent and the gas bubbles, thereby stabilizing the gas bubbles in the foam ink composition; and
depositing a continuous filament comprising the foam ink composition on a substrate,
wherein the depositing occurs in a controlled environment saturated with a vapor of the solvent.
2. The method of claim 1 , further comprising heating the continuous filament at an elevated temperature to sinter the stabilizing particles into a sintered material surrounding a population of pores created by the gas bubbles.
3. The method of claim 2 , wherein the foam ink composition further comprises fugitive particles comprising a polymer and/or carbon, and wherein heating the continuous filament at the elevated temperature further comprises forming an additional population of pores defined by the fugitive particles.
4. The method of claim 1 , wherein the foam ink composition further comprises a non-gelled polymer precursor, and further comprising, after extrusion and/or deposition of the continuous filament on the substrate, inducing gelation and/or crosslinking to form a polymer reinforcement structure in the continuous filament.
5. A 3D printed porous structure comprising:
a continuous filament comprising a foam ink composition comprising stabilizing particles and gas bubbles dispersed in a solvent, the stabilizing particles comprising a predetermined interfacial energy so as to exhibit a contact angle with the solvent of from about 15° to about 90°, and at least a portion of the stabilizing particles being positioned at interfacial regions between the solvent and the gas bubbles, thereby stabilizing the gas bubbles in the foam ink composition,
wherein the continuous filament has a tubular structure comprising a hollow core.
6. The 3D printed porous structure of claim 5 , further comprising a nonporous surface layer on the continuous filament.
7. A method of printing a porous structure, the method comprising:
extruding a foam ink composition through a nozzle and depositing a continuous filament comprising the foam ink composition on a substrate, the foam ink composition comprising stabilizing particles and gas bubbles dispersed in a solvent, the stabilizing particles comprising a predetermined interfacial energy so as to exhibit a contact angle with the solvent of from about 15° to about 90°, and at least a portion of the stabilizing particles being positioned at interfacial regions between the solvent and the gas bubbles, thereby stabilizing the gas bubbles in the foam ink composition; and
heating the continuous filament at an elevated temperature to sinter the stabilizing particles into a sintered material surrounding a population of pores created by the gas bubbles,
wherein the foam ink composition further comprises fugitive particles comprising a polymer and/or carbon, and wherein the heating further comprises forming an additional population of pores defined by the fugitive particles.