METHOD TO PRODUCE AGGREGATES FROM UNSETTLED CEMENTITIOUS MIXTURES
Method to produce aggregates from unsettled cementitious mixtures, comprising the steps of (a) adding at least one pelletizing agent to an unsettled cementitious mixture, (b) mixing constantly the mixture of step (a) in a mixer to produce pellets, (c) discharging the pellets obtained in step (b) and (d) drying the pellets formed in step (c). The pelletizing agent is selected from the group consisting of cellulose, chitosan, collagen, polyacrylamide and co-polymers of polyacrylamide and polyacrylics, polyamines, polyvinylalcohols, polysaccharides, lactic acid, methacrylic acid, methacrylate, hydroxyethyl, ethylene glycol, ethylene oxide, acrylic acid, inorganic flocculants and inorganic coagulants.
1 . Method to produce aggregates, comprising the steps of:
(a) adding at least one pelletizing agent to an unsettled cementitious mixture,
(b) mixing constantly the mixture of step (a) in a mixer to produce pellets,
(c) discharging the pellets obtained in step (b) and
(d) drying the pellets formed in step (c).
2 . Method according to claim 1 , wherein said method is to produce coarse aggregates and wherein the method comprises the steps of:
(a) adding at least one pelletizing agent to an unsettled cementitious mixture,
(b) mixing constantly the mixture of step (a) in a mixer to produce pellets,
(c) discharging the pellets obtained in step (b) to form a pile,
(d) drying the pellets formed in step (c) for a curing time of minimum t 1 to maximum t 2 depending on the curing temperature according to the following equations:
t 1= A×e −0.047×T(° C.)
t 2= B×e −0.047×T(° C.)
wherein A is a parameter from 50 to 55, B is a parameter from 75 to 80 and T(° C.) represents the curing temperature in Celsius degrees
and
(e) transforming the pile into a bed of dried pellets.
3 . Method according to claim 1 , wherein the solid active content of the pelletizing agent is at a concentration in the range of 0.2 to 10 kg/m 3 with respect to the unsettled cementitious mixture.
4 . Method according to claim 3 , wherein the solid active content of the pelletizing agent is at a concentration in the range of 0.8 to 10 kg/m 3 with respect to the unsettled cementitious mixture.
5 . Method according to claim 1 , wherein the pelletizing agent in step (a) is selected from the group consisting of cellulose, chitosan, collagen, polyacrylamide and co-polymers of polyacrylamide and polyacrylics, polyamines, polyvinylalcohols, polysaccharides, lactic acid, methacrylic acid, methacrylate, hydroxyethyl, ethylene glycol, ethylene oxide, acrylic acid, inorganic flocculants and inorganic coagulants.
6 . Method according to claim 1 , wherein the pelletizing agent is acrylamide-based.
7 . Method according to claim 1 , wherein the water-to-cement ratio of said unsettled cementitious mixture is between 0.15 and 1.5.
8 . Method according to claim 1 , wherein in step (b) mixing is carried out for 1 to 25 minutes.
9 . Method according to claim 8 , wherein mixing is carried out for 4 to 15 minutes.
10 . Method according to claim 8 , wherein mixing is carried out for 5 to 15 minutes.