Stabilized, pure lithium metal powder and method for producing the same
The invention relates to a stabilized lithium metal powder and to a method for producing the same, the stabilized, pure lithium metal powder having been passivated in an organic inert solvent under dispersal conditions with fatty acids or fatty acid esters according to the general formula (I) R—COOR′, in which R stands for C 10 -C 29 groups and R′ for H or C 1 -C 8 groups.
1. A method for preparing a stabilized lithium powder which does not show any run-away phenomenon when in contact with N-methyl-2-pyrrolidone having a water content of less than about 200 ppm at a minimum of 15 hours storage at 50° C., the method comprising:
reacting lithium metal having less than 200 ppm of metallic contamination above 180° C. in an organic, inert solvent under dispersal conditions with a passivation agent containing one or a plurality of fatty acids and/or one or a plurality of fatty acid esters according to formula I
R—COOR′ (I),
wherein R denotes C 10 -C 29 moieties and R′ stands for C 1 -C 8 moieties, wherein the passivation agent comprises an ethylate, a propanolate, and/or a butylate.
2. A method as in claim 1 further comprising prelithiating an electrochemically active material with the stabilized lithium metal powder.
3. A method according to claim 2 , wherein the electro-chemically active material is selected from the group consisting of graphite, alloy and a conversion anode for a lithium battery.
4. A method as in claim 1 wherein 0.1 g to 50 g of passivation agent is used per kg of lithium metal.
5. A method as in claim 1 further comprising applying a coating to the stabilized lithium metal powder at temperatures <180.5° C.
6. A method as in claim 1 wherein the organic, inert solvent is one or more hydrocarbons, selected from the group consisting of hexane, heptane, octane, decane, undecane, dodecane, toluene, ethyl benzene, cumene, and mixtures.