Extreme synthesis of crystalline aerogel materials from amorphous aerogel precursors
A method includes positioning a porous structure in a pressure cell; injecting an inert pressure medium within the pressure cell; and pressurizing the pressure cell to a pressure that thermodynamically favors a crystalline phase of the porous structure over an amorphous phase of the porous structure to transition the amorphous phase of the porous structure into the crystalline phase of the porous structure.
1. A method, comprising:
positioning a porous structure in a pressure cell;
injecting an inert pressure medium within the pressure cell; and
pressurizing the pressure cell to a pressure that thermodynamically favors a crystalline phase of the porous structure over an amorphous phase of the porous structure to transition the amorphous phase of the porous structure into the crystalline phase of the porous structure.
2. The method as recited in claim 1 , further comprising heating at least the amorphous phase of the porous structure to accelerate transition to the crystalline phase and to overcome a corresponding phase change barrier.
3. The method as recited in claim 2 , wherein a laser is selectively applied according to a user-defined pattern to heat one or more selected regions of the amorphous phase of the porous structure.
4. The method as recited in claim 2 , wherein the amorphous phase of the porous structure is heated to a temperature of greater than about 500° C.
5. The method as recited in claim 1 , further comprising returning the pressure and temperature in the pressure cell to ambient conditions.
6. The method as recited in claim 1 , wherein the amorphous phase of the porous structure comprises one of: silica aerogel, alumina aerogel, and titania aerogel.
7. The method as recited in claim 1 , wherein the amorphous phase of the porous structure is an aerogel of carbonized resorcinol-formaldehyde that has a specific density of about 30 to 50 mg/cm 3 .
8. The method as recited in claim 1 , wherein the amorphous phase of the porous structure comprises carbon aerogel and has a specific density of about 40 mg/cm 3 .
9. The method as recited in claim 1 , wherein the inert pressure medium conformally and homogeneously occupies a void volume of the pressure cell and a void volume of pores of the amorphous phase of the porous structure without disturbing pore morphology of the amorphous phase of the porous structure.
10. The method as recited in claim 1 , wherein the pressure cell is pressurized to a pressure of about 21×10 9 Pa, wherein the amorphous phase of the porous structure comprises an amorphous-phase carbonized resorcinol-formaldehyde aerogel.
11. The method as recited in claim 1 , wherein the inert pressure medium comprises at least one of: neon gas, argon gas, helium gas, krypton gas, xenon gas, and carbon dioxide gas.
12. The method as recited in claim 11 , wherein the inert pressure medium comprises supercritical neon gas.