Silicone hydrogels comprising N-alkyl methacrylamides and contact lenses made thereof
The present invention relates to silicone hydrogels exhibiting desired combinations of physical and mechanical properties, formed from a reactive monomer mixture comprising at least one N-alkyl methacrylamide, and at least one silicone-containing component. These silicone hydrogels may also contain hydrophilic components, crosslinking agents and toughening monomers. These silicone hydrogels are useful in preparing biomedical devices, ophthalmic lenses, and contact lenses.
1. A composite contact lens comprising a central region and a peripheral region wherein the central region comprises a first silicone hydrogel having a modulus between about 10,000 psi and about 200,000 psi and a water content of at least about 10%, formed from a reactive mixture comprising at least one N-alkyl methacrylamide, at least one silicone-containing component, and at least one silicone cross-linking agent containing between 5 and 200 siloxane repeat units; and the peripheral region comprising a second silicone hydrogel exhibiting a modulus between about 50 psi and about 300 psi.
2. The composite contact lens of claim 1 wherein the first silicone hydrogel comprises a water content of about 20 to about 40%.
3. The composite contact lens of claim 1 wherein the reactive mixture further comprises at least one photoinitiator.
4. The composite contact lens of claim 3 wherein said first silicone hydrogel is cured via exposure to light.
5. The composite contact lens of claim 1 wherein said silicone containing component comprises at least one silicone chain having 3-30 siloxane repeating units.
6. The composite contact lens of claim 5 wherein said at least one silicone chain is a polydialkyl siloxane chain.
7. The composite contact lens of claim 5 wherein said at least one silicone chain is a polydimethyl siloxane chain.
8. The composite contact lens of claim 5 wherein said at least one silicone chain is a polydiaryl siloxane chain.
9. The composite contact lens of claim 1 wherein said reactive mixture comprises about 20 to about 60 wt % of said silicone containing component, based upon all reactive components.
10. The composite contact lens of claim 1 wherein said reactive mixture comprises about 5 wt % to about 50 wt % of at least one N-alkyl methacrylamide, based upon all reactive components.
11. The composite contact lens of claim 1 wherein said silicone-containing component is selected from compounds of Formulae I through V, and combinations thereof:
wherein R 1 is a hydrogen atom or methyl; Z is selected from O, N, S or NCH 2 CH 2 O; when Z═O or S, R 2 is not required; wherein j is a whole number between 1 and 20; q is 1 to 50; and n 1 and n 2 are between 4 to 100; n 3 is 1-50;
wherein R 2 is H or is a linear, branched, or cyclic alkyl group containing one to eight carbon atoms, any of which may be further substituted with at least one hydroxy group, and which may be optionally substituted with amide, ether, and combinations thereof;
wherein R 3 is a substituted or unsubstituted C1-6 alkylene segment of formula (CH 2 ) r where each methylene group is optionally independently substituted with ethers, amines, carbonyls, carboxylates, carbamates and combinations thereof; or an oxyalkylene segment (OCH 2 ) k and k is a whole number from one to three, or wherein R 3 may be a mixture of alkylene and oxyalkylene segments and the sum of r and k is between 1 and 9;
wherein each R 4 is independently a linear, branched, or cyclic alkyl group containing between one and six carbon atoms, a linear, branched, or cyclic alkoxy group containing between one and six carbon atoms, a linear or branched polyethyleneoxyalkyl group, a phenyl group, a benzyl group, a substituted or un-substituted aryl group, a fluoroalkyl group, a partially fluorinated alkyl group, a perfluoroalkyl group, a fluorine atom, or combinations thereof;
wherein R 5 is a substituted or un-substituted linear or branched alkyl group having 1 to eight carbon atoms; or an aryl group, any of which may be substituted with one or more fluorine atoms.
12. The composite contact lens of claim 1 wherein said N-alkyl methacrylamide is N-methyl methacrylamide.
13. The composite contact lens of claim 1 wherein said reactive mixture comprises about 7 to about 30 wt % of at least one N-alkyl methacrylamide, based upon all reactive components.
14. The composite contact lens of claim 1 wherein the first silicone hydrogel further comprises at least one toughening agent.
15. The composite contact lens of claim 14 wherein the toughening agent is selected from the group consisting of methyl methacrylate, tert-butyl methacrylate, isobornyl methacrylate, cyclohexyl methacrylate, styrene, substituted styrenes, N-4-vinylbenzyl-N-alkyl acetamides, N-4-vinylbenzyl pyrrolidone, and mixtures thereof.
16. The composite contact lens of claim 1 wherein the first and second silicone hydrogels comprise water contents within about 5 weight percent of one another.
17. The composite contact lens of claim 1 wherein the central region is encapsulated by the peripheral region.