Binder composition for improved tack coat and stress absorbing membrane interlayer application for road construction
A binder composition for asphalt pavements that includes: an asphalt binder; an elastomeric polymer; a wax modifier; and optionally at least one of: i) fumed silica or fumed alumina; and ii) a saponified fatty acid and a resin acid gelling compound. The composition is applied as a tack coat and/or a stress absorbing membrane interlayer and is non-tracking.
1. A non-tracking tack coat or stress absorbing membrane interlayer formed on pavement surface which non-tracking tack coat or stress absorbing membrane interlayer is applied across the entire width of the pavement surface as a binder composition that comprises:
an asphalt binder;
an elastomeric polymer,
a wax modifier; and
at least one of:
i) fumed silica or fumed alumina; and
ii) a saponified fatty acid and a resin acid gelling compound,
wherein the asphalt binder comprises 85 to 97 wt. % of the binder composition.
2. A non-tracking tack coat or stress absorbing membrane interlayer according to claim 1 , wherein the binder composition comprises fumed silica or fumed alumina which imparts a non-tacky character to the binder composition.
3. A non-tracking tack coat or stress absorbing membrane interlayer according to claim 1 , wherein the binder composition is applied on the pavement surface at an application rate of 0.15 to 0.6 gallon per square yard.
4. A non-tracking tack coat or stress absorbing membrane interlayer according to claim 1 , wherein the binder composition is applied on the pavement surface at an application rate of 0.10 to 0.15 gallon per square yard.
5. A non-tracking tack coat or stress absorbing membrane interlayer according to claim 1 , wherein the pavement surface comprises one of asphalt concrete, Portland cement concrete, milled asphalt concrete or Portland cement concrete or brick or chip seal surface.
6. A non-tracking tack coat or stress absorbing membrane interlayer according to claim 1 having an asphalt pavement layer formed thereon.
7. A method of installing an asphalt pavement which comprises:
providing a surface to be paved,
applying a non-tracking layer of a binder composition across the entire width of the surface to be paved, which binder composition comprises:
an asphalt binder;
an elastomeric polymer; and
a wax modifier; and
at least one of:
i) fumed silica or fumed alumina; and
ii) a saponified fatty acid and a resin acid gelling compound,
wherein the asphalt binder comprises 85 to 97 wt. % of the binder composition, and
applying a hot-mix asphalt layer over the binder layer to form an asphalt pavement.
8. The method of installing an asphalt pavement according to claim 7 , wherein the binder composition is applied as a tack coat.
9. The method of installing an asphalt pavement according to claim 8 , wherein the binder composition is applied on the surface at an application rate of 0.10 to 0.15 gallon per square yard.
10. The method of installing an asphalt pavement according to claim 7 , wherein the binder composition is applied as a stress absorbing membrane interlayer.
11. The method of installing an asphalt pavement according to claim 7 , wherein the binder composition is applied on the surface at an application rate of 0.15 to 0.6 gallon per square yard.
12. The method of installing an asphalt pavement according to claim 7 , wherein the surface comprises one of asphalt concrete, Portland cement concrete, milled asphalt concrete or Portland cement concrete or brick or chip seal surface.
13. The method of installing an asphalt pavement according to claim 7 , wherein the hot-mix asphalt layer is applied over the binder layer without an intermediate layer.
14. The method of installing an asphalt pavement according to claim 7 , wherein the binder composition comprises fumed silica or fumed alumina which imparts a non-tacky characteristic to the binder composition.