Gypsum fiber board and method for producing gypsum fiber boards
A gypsum fiber board produced in a Siempelkamp dry-process, comprising 75 wt % to 90 wt % (relative to the total dry mix) of calcium sulfate hemi-hydrate and 10 wt % to 25 wt % (relative to the total dry mix) paper fibers, wherein the calcium sulfate hemi-hydrate is a mixture of α-calcium sulfate hemi-hydrate and β-calcium sulfate hemi-hydrate, wherein the content of α-calcium sulfate hemi-hydrate in the mixture is at least 5 wt % (relative to the total calcium sulfate hemi-hydrate) is disclosed. Also disclosed is a method for producing a gypsum fiber board of a thickness of 23 mm in a Siempelkamp dry-process.
1. A method for producing gypsum fiber boards, comprising the steps of:
preparing a compressible mat of gypsum-containing material from a mixture comprising 75 wt % to 90 wt %, relative to the total dry mix, of calcium sulfate hemi-hydrate and 10 wt % to 25 wt %, relative to the total dry mix, of paper fibers, wherein the calcium sulfate hemi-hydrate is a mixture of α-calcium sulfate hemi-hydrate and β-calcium sulfate hemi-hydrate, wherein the content of α-calcium sulfate hemi-hydrate in the mixture is at least 10 wt %, relative to the total calcium sulfate hemi-hydrate;
moving the dry compressible mat of gypsum-containing material on a conveyor belt to a hydration water tank, and
hydrating the gypsum-containing material with hydration water added from above to the top surface of the mat in excess prior to passing the gypsum-containing material through a continuous press to form an endless gypsum fiber board having a thickness greater than 19 mm.
2. The method according to claim 1 , wherein the step of preparing the compressible mat comprises mixing at least 20 wt %, relative to the total calcium sulfate hemi-hydrate, of α-calcium sulfate hemi-hydrate, with a least 50 wt %, relative to the total calcium sulfate hemi-hydrate, of β-calcium sulfate hemi-hydrate.
3. The method according to claim 1 , further comprising a step of adding a citric acid retardant, and/or a step of adding a coated dihydrate accelerator.
4. The method according to claim 1 , wherein the granulation of at least 90% of the gypsum fiber composition is above 1 μm.
5. The method according to claim 1 , wherein the thickness of the dry compressible mat of gypsum-containing material prior to adding water is within the range of 80 mm to 100 mm.