Conductive polymer and Si nanoparticles composite secondary particles and structured current collectors for high loading lithium ion negative electrode application
Embodiments of the present invention disclose a composition of matter comprising a silicon (Si) nanoparticle coated with a conductive polymer. Another embodiment discloses a method for preparing a composition of matter comprising a plurality of silicon (Si) nanoparticles coated with a conductive polymer comprising providing Si nanoparticles, providing a conductive polymer, preparing a Si nanoparticle, conductive polymer, and solvent slurry, spraying the slurry into a liquid medium that is a non-solvent of the conductive polymer, and precipitating the silicon (Si) nanoparticles coated with the conductive polymer. Another embodiment discloses an anode comprising a current collector, and a composition of matter comprising a silicon (Si) nanoparticle coated with a conductive polymer.
1. A battery comprising:
a cathode; and
an anode comprising:
a current collector; and
a composition of matter comprising a silicon (Si) nanoparticle coated with a conductive polymer, wherein the conductive polymer is poly(9,9-dioctylfluorene-co-fluorenone) (PFFO), poly(9,9-dioctylfluorene-co-fluorenone-co-methylbenzoic acid) (PFFOMB), or poly(9,9-dioctylfluorene-co-fluorenone-co-benzoic acid) (PFFOBA).
2. The battery of claim 1 , wherein the current collector comprises projections perpendicular to a base.
3. The battery of claim 1 , wherein the current collector comprises copper (Cu).
4. The battery of claim 1 , wherein the conductive polymer is poly(9,9-dioctylfluorene-co-fluorenone-co-methylbenzoic acid) (PFFOMB).
5. The battery of claim 1 , wherein the conductive polymer is poly(9,9-dioctylfluorene-co-fluorenone) (PFFO).
6. The battery of claim 1 , wherein the conductive polymer is poly(9,9-dioctylfluorene-co-fluorenone-co-benzoic acid) (PFFOBA).
7. The battery of claim 1 , wherein a weight ratio of the conductive polymer to Si nanoparticle ranges from 0.01 to 100.
8. The battery of claim 1 , wherein the Si nanoparticle is n-doped or p-doped.
9. The battery of claim 1 , wherein a porosity of the composition of matter ranges from 1% to 70% void space.
10. The battery of claim 1 , wherein the silicon (Si) nanoparticle coated with the conductive polymer forms a secondary particle.
11. The battery of claim 10 , wherein the secondary particle can be spherical, two-dimensional plates, or fibers.
12. The battery of claim 11 , wherein a dimension of the secondary particle ranges from 1 nm to 1000 μm in diameter.
13. The battery of claim 11 , wherein dimensions of the fiber secondary particle range from 1 nm to 1000 μm in diameter and 2 nm to 10000 μm in length.
14. The battery of claim 11 wherein dimensions of the two-dimensional plate secondary particle range from 1 nm to 1000 μm in thickness and 2 nm to 5000 μm in length.